Semiconductor device

ABSTRACT

A semiconductor device includes a gate electrode, a gate insulating film which includes oxidized material containing silicon and covers the gate electrode, an oxide semiconductor film provided to be in contact with the gate insulating film and overlap with at least the gate electrode, and a source electrode and a drain electrode electrically connected to the oxide semiconductor film. In the oxide semiconductor film, a first region which is provided to be in contact with the gate insulating film and have a thickness less than or equal to 5 nm has a silicon concentration lower than or equal to 1.0 at. %, and a region in the oxide semiconductor film other than the first region has lower silicon concentration than the first region. At least the first region includes a crystal portion.

TECHNICAL FIELD

The present invention relates to a semiconductor device and a method formanufacturing the semiconductor device.

In this specification, a semiconductor device generally means a devicewhich can function by utilizing semiconductor characteristics, and anelectrooptic device, a semiconductor circuit, and electronic equipmentare all semiconductor devices.

BACKGROUND ART

A technique by which a transistor is formed using a semiconductor thinfilm formed over a substrate having an insulating surface has attractedattention. The transistor is applied to a wide range of electronicdevices such as an integrated circuit (IC) or an image display device(display device). A silicon-based semiconductor material is widely knownas a material for a semiconductor thin film applicable to a transistor.As another material, an oxide semiconductor has been attractingattention.

For example, a transistor whose active layer includes an amorphous oxideincluding indium (In), gallium (Ga), and zinc (Zn) is disclosed (seePatent Document 1).

Transistors including oxide semiconductors have on-state characteristics(e.g., on-state current) superior to those of transistors includingamorphous silicon. In order to apply the transistors including oxidesemiconductors to high-performance devices, such transistors arerequired to have further improved characteristics, and thus techniquesof crystallization of oxide semiconductors have been developed (PatentDocument 2). In Patent Document 2, a technique in which an oxidesemiconductor is crystallized by heat treatment is disclosed.

REFERENCE Patent Document

-   [Patent Document 1] Japanese Published Patent Application No.    2006-165528-   [Patent Document 2] Japanese Published Patent Application No.    2008-311342

DISCLOSURE OF INVENTION

An oxide semiconductor film used in a transistor is formed by asputtering method in many cases. However, when the oxide semiconductorfilm is formed by sputtering, in some cases, an ionized rare gas elementor a particle ejected from a surface of a target flicks off a particleof a film, such as a gate insulating film, on which the oxidesemiconductor film is to be formed (the film is also referred to as“formed film”). Particles flicked off from the formed film enter theoxide semiconductor film and functions as an impurity element therein.In particular, the oxide semiconductor film in the vicinity of a surfaceof the formed film (the surface is also referred to as “formed filmsurface”) may have high concentration of the impurity element. Further,when the impurity element is left in the oxide semiconductor film in thevicinity of the formed film surface, the impurity element causesadversely effect on characteristics of the transistor.

Furthermore, the impurity element included in the oxide semiconductorfilm in the vicinity of the formed film surface inhibits crystallizationof the oxide semiconductor film. As a result, an amorphous region isleft in the oxide semiconductor film in the vicinity of the formed filmsurface.

Thus, the following countermeasure can be considered: the oxidesemiconductor film is made thick, and a crystal region formed in asurface layer is used. However, in order to reduce parasitic capacitanceand to operate the transistor with lower power, the oxide semiconductorfilm is desirably formed thin. In that case, a channel formation regionis formed in the oxide semiconductor film in the vicinity of the formedfilm surface, and crystallization of the oxide semiconductor film isdesirably progressed in the vicinity of the formed film surfaceaccordingly.

In view of the above problem, an object is to reduce the concentrationof impurities included in an oxide semiconductor film in the vicinity ofthe formed film surface. Further, an object is to improve crystallinityof the oxide semiconductor film. Further, an object is to provide asemiconductor device having stable electric characteristics with use ofthe oxide semiconductor film.

One embodiment of the disclosed invention is a semiconductor deviceincluding an insulating film which includes oxidized material containingsilicon, an oxide semiconductor film provided to be in contact with theinsulating film, a source electrode and a drain electrode electricallyconnected to the oxide semiconductor film, and a gate electrode adjacentto the oxide semiconductor film. The oxide semiconductor film includes afirst region in which a concentration of silicon distributed from aninterface with the gate insulating film toward an inside of the oxidesemiconductor film is lower than or equal to 1.0 at. %, and at least thefirst region includes a crystal portion. The gate electrode may belocated below the oxide semiconductor film with the insulating filminterposed therebetween.

One embodiment of the disclosed invention is a semiconductor deviceincluding a gate electrode, a gate insulating film which includesoxidized material containing silicon and covers the gate electrode, anoxide semiconductor film provided to be in contact with the gateinsulating film and overlap with at least the gate electrode, a channelprotective film provided to be in contact with the oxide semiconductorfilm, and a source electrode and a drain electrode which are providedover the channel protective film and electrically connected to the oxidesemiconductor film. The oxide semiconductor film includes a first regionin which a concentration of silicon distributed from an interface withthe gate insulating film toward an inside of the oxide semiconductorfilm is lower than or equal to 1.0 at. %, and at least the first regionincludes a crystal portion.

In each of the above structures, the first region is preferably providedto be in contact with the gate insulating film or the insulating filmand have a thickness less than or equal to 5 nm, and the concentrationof silicon included in a region other than the first region ispreferably lower than the concentration of silicon included in the firstregion.

In each of the above structures, the region in the oxide semiconductorfilm other than the first region preferably includes a crystal portion.

Further, one embodiment of the disclosed invention is a semiconductordevice including a gate electrode, a gate insulating film which includesoxidized material containing silicon and covers the gate electrode, anoxide semiconductor film provided to be in contact with the gateinsulating film and overlap with at least the gate electrode, a sourceelectrode and a drain electrode electrically connected to the oxidesemiconductor film, and a protective insulating film which includesoxidized material containing silicon and covers the oxide semiconductorfilm and the source electrode and the drain electrode. The oxidesemiconductor film includes a first region in which a concentration ofsilicon distributed from an interface with the gate insulating filmtoward an inside of the oxide semiconductor film is lower than or equalto 1.0 at. %. The oxide semiconductor film includes a second region inwhich a concentration of silicon distributed from an interface with theprotective insulating film toward the inside of the oxide semiconductorfilm is lower than or equal to 1.0 at. %. At least the first region andthe second region include a crystal portion.

In each of the above structures, the first region is preferably providedto be in contact with the gate insulating film and have a thickness lessthan or equal to 5 nm, the second region is preferably provided to be incontact with the protective insulating film and have a thickness lessthan or equal to 5 nm, and the concentration of silicon included in aregion other than the first region and the second region is preferablylower than the concentrations of silicon included in the first regionand the second region.

Further, in each of the above structures, a crystal portion ispreferably included in the region in the oxide semiconductor film otherthan the first region and the second region.

Further, in each of the above structures, a c-axis of the crystalportion is preferably aligned in a direction perpendicular to theinterface between the oxide semiconductor film and the gate insulatingfilm or the insulating film.

Further, in each of the above structures, the concentration of siliconincluded in the first region is preferably lower than or equal to 0.1at. %.

Further, in each of the above structures, the gate insulating film orthe insulating film includes carbon, and the concentration of carbon inthe first region is preferably lower than or equal to 1.0×10²⁰atoms/cm³.

According to one embodiment of the disclosed invention, theconcentration of impurities included in the oxide semiconductor film inthe vicinity of the formed film surface can be reduced. In addition,crystallinity of the oxide semiconductor film can be improved. Thus,with use of such an oxide semiconductor film, a semiconductor devicehaving stable electric characteristics can be provided.

BRIEF DESCRIPTION OF DRAWINGS

FIGS. 1A and 1B are a plan view and a cross-sectional view illustratingone embodiment of a semiconductor device.

FIGS. 2A and 2B are a plan view and a cross-sectional view illustratingone embodiment of a semiconductor device.

FIGS. 3A and 3B are a plan view and a cross-sectional view illustratingone embodiment of a semiconductor device.

FIGS. 4A to 4E are cross-sectional views illustrating an example of amanufacturing process of a semiconductor device.

FIGS. 5A to 5E are cross-sectional views illustrating an example of amanufacturing process of a semiconductor device.

FIG. 6 is a model diagram used for calculation.

FIGS. 7A to 7C show calculation results.

FIGS. 8A to 8C show calculation results.

FIGS. 9A to 9C illustrate one embodiment of a semiconductor device.

FIG. 10 illustrates one embodiment of a semiconductor device.

FIG. 11 illustrates one embodiment of a semiconductor device.

FIG. 12 illustrates one embodiment of a semiconductor device.

FIGS. 13A to 13F each illustrate an electronic device.

FIG. 14 is a graph showing measurement results according to one exampleof the present invention.

FIG. 15 illustrates a structure of a sample according to one example ofthe present invention.

FIG. 16 is a graph showing measurement results according to one exampleof the present invention.

FIG. 17 illustrates a structure of a sample according to one example ofthe present invention.

FIGS. 18A and 18B are graphs showing measurement results according toone example of the present invention.

FIGS. 19A and 19B each illustrate a structure of a sample according toone example of the present invention.

FIGS. 20A and 20B are graphs showing measurement results according toone example of the present invention.

FIGS. 21A and 21B are model diagrams used for calculation.

FIGS. 22A and 22B are model diagrams used for calculation.

FIG. 23 shows calculation results.

FIGS. 24A and 24B are model diagrams used for calculation.

FIG. 25 shows calculation results.

BEST MODE FOR CARRYING OUT THE INVENTION

Hereinafter, embodiments of the invention disclosed in thisspecification will be described in detail with reference to theaccompanying drawings. Note that the present invention is not limited tothe following description and it will be readily appreciated by thoseskilled in the art that modes and details can be modified in variousways without departing from the spirit and the scope of the presentinvention. Therefore, the invention should not be construed as beinglimited to the description in the following embodiments.

Note that the position, the size, the range, or the like of eachstructure illustrated in the drawings and the like are not accuratelyrepresented in some cases for easy understanding. Therefore, thedisclosed invention is not necessarily limited to the position, size,range, or the like as disclosed in the drawings and the like.

In this specification and the like, ordinal numbers such as “first”,“second”, and “third” are used in order to avoid confusion amongcomponents, and the terms do not mean limitation of the number ofcomponents.

Note that in this specification and the like, the term such as “over” or“below” does not necessarily mean that a component is placed “directlyon” or “directly under” another component. For example, the expression“a gate electrode over a gate insulating layer” can mean the case wherethere is an additional component between the gate insulating layer andthe gate electrode.

In addition, in this specification and the like, the term such as“electrode” or “wiring” does not limit a function of a component. Forexample, an “electrode” is sometimes used as part of a “wiring”, andvice versa. Furthermore, the term “electrode” or “wiring” can includethe case where a plurality of “electrodes” or “wirings” is formed in anintegrated manner.

Functions of a “source” and a “drain” are sometimes replaced with eachother when a transistor of opposite polarity is used or when thedirection of current flowing is changed in circuit operation, forexample. Therefore, the terms “source” and “drain” can be replaced witheach other in this specification and the like.

Note that in this specification and the like, the term “electricallyconnected” includes the case where components are connected through anobject having any electric function. There is no particular limitationon an object having any electric function as long as electric signalscan be transmitted and received between components that are connectedthrough the object. Examples of an “object having any electric function”are a switching element such as a transistor, a resistor, an inductor, acapacitor, and an element with a variety of functions as well as anelectrode and a wiring.

Embodiment 1

In this embodiment, one embodiment of a semiconductor device and amanufacturing method thereof will be described with reference to FIGS.1A and 1B, FIGS. 2A and 2B, FIGS. 3A and 3B, FIGS. 4A to 4E, and FIGS.5A to 5E.

<Example of Structure of Semiconductor Device>

In FIGS. 1A and 1B, a plan view and a cross-sectional view of achannel-etched type transistor, which has a bottom-gate structure, areshown as an example of a semiconductor device. FIG. 1A is a plan viewand FIG. 1B is a cross-sectional view taken along line A-B in FIG. 1A.In FIG. 1A, some of components (e.g., a protective insulating film 109or the like) of a transistor 110 are omitted to avoid complexity.

The transistor 110 illustrated in FIGS. 1A and 1B includes, over asubstrate 100 having an insulating surface, a gate electrode 101, a gateinsulating film 102 covering the gate electrode 101, an oxidesemiconductor film 103 provided to be in contact with the gateinsulating film 102 and overlap with at least the gate electrode 101, asource electrode 105 a and a drain electrode 105 b electricallyconnected to the oxide semiconductor film 103, and the protectiveinsulating film 109 covering the oxide semiconductor film 103 and thesource electrode 105 a and the drain electrode 105 b.

The thickness of the oxide semiconductor film 103 is greater than 5 nmand less than or equal to 200 nm, preferably greater than or equal to 10nm and less than or equal to 30 nm. Further, the oxide semiconductorfilm 103 preferably has a structure with crystallinity (e.g., a singlecrystal structure, a microcrystalline structure, or the like).

In this embodiment, the oxide semiconductor film 103 is preferably ac-axis aligned crystalline oxide semiconductor (CAAC-OS) film.

The CAAC-OS film is not completely single crystal or completelyamorphous. The CAAC-OS film is an oxide semiconductor film with acrystal-amorphous mixed phase structure where crystal portions areincluded in an amorphous phase. Note that in most cases, the crystalportion fits inside a cube whose one side is less than 100 nm. From anobservation image obtained with a transmission electron microscope(TEM), a boundary between an amorphous region and a crystal region inthe CAAC-OS film is not clear. Further, with the TEM, a grain boundaryin the CAAC-OS film cannot be found. Thus, in the CAAC-OS film, areduction in electron mobility, due to the grain boundary, issuppressed.

In each of the crystal portions included in the CAAC-OS film, a c-axisis aligned in a direction perpendicular to a surface where the CAAC-OSfilm is formed or a surface of the CAAC-OS film, triangular or hexagonalatomic arrangement which is seen from the direction perpendicular to thea-b plane is formed, and metal atoms are arranged in a layered manner ormetal atoms and oxygen atoms are arranged in a layered manner when seenfrom the direction perpendicular to the c-axis. Note that, among crystalportions, the directions of an a-axis and a b-axis of one crystalportion may be different from those of another crystal portion. In thisspecification and the like, a simple term “perpendicular” includes arange from 85° to 95°.

In the CAAC-OS film, distribution of crystal portions is not necessarilyuniform. For example, in the formation process of the CAAC-OS film, inthe case where crystal growth occurs from a surface side of the oxidesemiconductor film, the proportion of crystal portions in the vicinityof the surface of the oxide semiconductor film is higher than that inthe vicinity of the surface where the oxide semiconductor film is formedin some cases.

Since the c-axes of the crystal portions included in the CAAC-OS filmare aligned in the direction perpendicular to a surface where theCAAC-OS film is formed or a surface of the CAAC-OS film, the directionsof the c-axes may be different from each other depending on the shape ofthe CAAC-OS film (the cross-sectional shape of the surface where theCAAC-OS film is formed or the cross-sectional shape of the surface ofthe CAAC-OS film). Note that when the CAAC-OS film is formed, thedirection of c-axis of the crystal portion is the directionperpendicular to the surface where the CAAC-OS film is formed or thesurface of the CAAC-OS film. The crystal portion is formed by filmformation or by performing treatment for crystallization such as heattreatment after film formation.

With use of the CAAC-OS film in a transistor, change in electriccharacteristics of the transistor due to irradiation with visible lightor ultraviolet light can be reduced. Change and variation in thresholdvoltages can be suppressed. Thus, the transistor has high reliability.

In an oxide semiconductor having crystallinity (crystalline oxidesemiconductor), defects in the bulk can be further reduced. Further,when planarity of the surface of the crystalline oxide semiconductorfilm is enhanced, a transistor including such an oxide semiconductor canobtain higher field-effect mobility than a transistor including anamorphous oxide semiconductor. In order to enhance the surface planarityof the oxide semiconductor film, the oxide semiconductor is preferablyformed over a flat surface. Specifically, the oxide semiconductor ispreferably formed over a surface with an average surface roughness(R_(a)) less than or equal to 0.15 nm, preferably less than or equal to0.1 nm.

Note that the average surface roughness (R_(a)) is obtained byexpanding, into three dimensions, arithmetic mean surface roughness thatis defined by HS B 0601:2001 (ISO4287:1997) so as to be able to apply itto a curved surface. R_(a) can be expressed as an “average value of theabsolute values of deviations from a reference surface to a specificsurface” and is defined by the following formula.

$\begin{matrix}{{Ra} = \left. {\frac{1}{S_{0}}{\int_{y_{1}}^{y_{2}}\int_{x_{1}}^{x_{2}}}} \middle| {{f\left( {x,y} \right)} - Z_{0}} \middle| {dxdy} \right.} & \left\lbrack {{FORMULA}\mspace{14mu} 1} \right\rbrack\end{matrix}$

Here, the specific surface is a surface that is a target of roughnessmeasurement, and is a quadrilateral region specified by four pointsrepresented by the coordinates (x₁, y₁), f(x₁, y₁)), (x₁, y₂, f(x₁,y₂)), (x₂, y₁, f(x₂, y₁)), and (x₂, y₂, f(x₂, y₂)). Moreover, S₀represents the area of a rectangle which is obtained by projecting thespecific surface on the xy plane, and Z₀ represents the height of thereference surface (the average height of the specific surface). R_(a)can be measured using an atomic force microscope (AFM).

As illustrated in FIG. 1B, an end portion of the oxide semiconductorfilm 103 is preferably tapered at an angle of 20° to 50°. When the oxidesemiconductor film 103 has a perpendicular end portion, oxygen is morelikely to be released from the oxide semiconductor film 103, andaccordingly, oxygen vacancies are likely to be generated. When the oxidesemiconductor film 103 has a tapered end portion, generation of oxygenvacancies is suppressed, and thus generation of leakage current of thetransistor 110 can be reduced.

An oxide semiconductor used for the oxide semiconductor film 103preferably contains at least indium (In) or zinc (Zn). In particular, Inand Zn are preferably contained. In addition, as a stabilizer forreducing variation in electric characteristics of a transistor using theoxide semiconductor, one or more selected from gallium (Ga), tin (Sn),hafnium (Hf), zirconium (Zr), titanium (Ti), scandium (Sc), yttrium (Y),and an lanthanoid element (such as cerium (Ce), neodymium (Nd), orgadolinium (Gd), for example) is preferably contained.

As the oxide semiconductor, for example, any of the following can beused: indium oxide; tin oxide; zinc oxide; a two-component metal oxidesuch as an In—Zn-based oxide, a Sn—Zn-based oxide, an Al—Zn-based oxide,a Zn—Mg-based oxide, a Sn—Mg-based oxide, an In—Mg-based oxide, or anIn—Ga-based oxide; a three-component metal oxide such as anIn—Ga—Zn-based oxide (also referred to as IGZO), an In—Al—Zn-basedoxide, an In—Sn—Zn-based oxide, a Sn—Ga—Zn-based oxide, anAl—Ga—Zn-based oxide, a Sn—Al—Zn-based oxide, an In—Hf—Zn-based oxide,an In—Zr—Zn-based oxide, an In—Ti—Zn-based oxide, an In—Sc—Zn-basedoxide, an In—Y—Zn-based oxide, an In—La—Zn-based oxide, anIn—Ce—Zn-based oxide, an In—Pr—Zn-based oxide, an In—Nd—Zn-based oxide,an In—Sm—Zn-based oxide, an In—Eu—Zn-based oxide, an In—Gd—Zn-basedoxide, an In—Tb—Zn-based oxide, an In—Dy—Zn-based oxide, anIn—Ho—Zn-based oxide, an In—Er—Zn-based oxide, an In—Tm—Zn-based oxide,an In—Yb—Zn-based oxide, or an In—Lu—Zn-based oxide; and afour-component metal oxide such as an In—Sn—Ga—Zn-based oxide, anIn—Hf—Ga—Zn-based oxide, an In—Al—Ga—Zn-based oxide, anIn—Sn—Al—Zn-based oxide, an In—Sn—Hf—Zn-based oxide, or anIn—Hf—Al—Zn-based oxide.

Here, an “In—Ga—Zn-based oxide” means an oxide containing In, Ga, and Znas its main components and there is no particular limitation on theratio of In:Ga:Zn. The In—Ga—Zn-based oxide may contain a metal elementother than In, Ga, and Zn.

Alternatively, a material represented by InMO₃(ZnO)_(m) (m>0 issatisfied, and m is not an integer) may be used as an oxidesemiconductor. Note that M represents one or more metal elementsselected from Ga, Fe, Mn, and Co, or the above-described element as astabilizer. Alternatively, as the oxide semiconductor, a materialrepresented by a chemical formula, In₂SnO₅(ZnO)_(n) (n>0, n is a naturalnumber) may be used.

For example, an In—Ga—Zn-based oxide with an atomic ratio ofIn:Ga:Zn=1:1:1, In:Ga:Zn=3:1:2, or In:Ga:Zn=2:1:3, or any of oxideswhose composition is in the neighborhood of the above compositions canbe used.

For the gate insulating film 102, an oxide insulating film having asufficient withstand voltage and sufficient insulating properties ispreferably used. In the case where the gate insulating film 102 has asingle-layer structure, an insulating film including oxidized materialcontaining silicon, such as silicon oxide, may be used for example.

Alternatively, the gate insulating film 102 may have a stackedstructure. In the case where the gate insulating film 102 has a stackedstructure, silicon oxide may be stacked over gallium oxide, aluminumoxide, silicon nitride, silicon oxynitride, aluminum oxynitride, yttriumoxide, lanthanum oxide, silicon nitride oxide, or the like.Alternatively, silicon oxide may be stacked over a high-k material suchas hafnium oxide, hafnium silicate (HfSi_(x)O_(y) (x>0, y>0)), hafniumsilicate to which nitrogen is added (HfSiO_(x)N_(y) (x>0, y>0)), orhafnium aluminate (HfAl_(x)O_(y) (x>0, y>0)). The use of such a high-kmaterial enables a reduction in gate leakage current.

In the case of using an oxide insulating film as the gate insulatingfilm 102, part of contained oxygen can be released from the oxideinsulating film when the oxide insulating film is heated; thus, oxygencan be supplied to the oxide semiconductor film 103, and oxygenvacancies in the oxide semiconductor film 103 can be filled. Inparticular, the gate insulating film 102 preferably contains a largeamount of oxygen which exceeds at least the stoichiometry in (a bulk of)the film. For example, a film of silicon oxide represented by theformula SiO_(2+α) (α>0) is preferably used as the gate insulating film102. When such a silicon oxide film is used as the gate insulating film102, oxygen can be supplied to the oxide semiconductor film 103, so thatthe transistor 110 using the oxide semiconductor film 103 can havefavorable transistor characteristics.

However, in the case of using a silicon oxide film as the gateinsulating film 102, silicon in the gate insulating film 102 might betaken as an impurity into the oxide semiconductor film 103. Silicon orthe like enters the oxide semiconductor film 103 and serves as animpurity, which affects characteristics of the transistor. Further, whenan impurity element enters the oxide semiconductor film 103 in thevicinity of the surface on which the oxide semiconductor film 103 isformed (formed film surface), crystallization of an oxide semiconductorfilm is inhibited by the impurity element. Thus, an amorphous region isleft in the oxide semiconductor film in the vicinity of the formed filmsurface. In addition, in the case where the oxide semiconductor film 103is a CAAC-OS film, it is difficult to form a crystal portion in thevicinity of the formed film surface.

In particular, impurities such as silicon are likely to enter the oxidesemiconductor film 103 in the vicinity of the formed film surface wherethe oxide semiconductor film 103 and the gate insulating film 102 are incontact with each other. A channel formation region of the transistor110 is formed in the oxide semiconductor film 103 in the vicinity of theformed film surface; thus, when impurities such as silicon enter thevicinity of the formed film surface, characteristics of the transistor110 might be changed.

Change in structure of the oxide semiconductor film 103 when SiO₂,oxidized material containing silicon, is added as an impurity wasexamined by classical molecular dynamics calculation. The resultsthereof are described with reference to FIGS. 21A and 21B, FIGS. 22A and22B, FIG. 23, FIGS. 24A and 24B, and FIG. 25. Note that simulationsoftware “SCIGRESS ME” manufactured by Fujitsu Limited was used forclassical molecular dynamics calculation. An empirical potential whichcharacterizes the interaction between atoms is defined in the classicalmolecular dynamics method, so that force that acts on each atom isevaluated. Newton's equation of motion is numerically solved, wherebymotion (time-dependent change) of each atom can be deterministicallytracked.

Hereinafter, calculation models and calculation conditions aredescribed. Note that in this calculation, the Born-Mayer-Hugginspotential was used.

A single crystal structure of InGaZnO₄ including 1680 atoms (see FIG.21A) and a structure of InGaZnO₄ including 1680 atoms in which 20 atomsof each of In, Ga, and Zn are substituted by silicon (Si) atoms (seeFIG. 21B) were formed as calculation models. In the model of Sisubstitution shown in FIG. 21B, silicon atoms are included at 3.57 at. %(2.34 wt. %). Further, the density of the model of the single crystalshown in FIG. 21A is 6.36 g/cm³, and the density of the model of Sisubstitution shown in FIG. 21B is 6.08 g/cm³.

At 1727° C. which is lower than the melting point of the InGaZnO₄ singlecrystal (about 2000° C. according to estimation by the classicalmolecular dynamics calculation), structure relaxation was performed onthe calculation models shown in FIGS. 21A and 21B by the classicalmolecular dynamics calculation at a fixed pressure (1 atm) for 150 psec(time step width 0.2 fsec×750000 steps). The radial distributionfunctions g(r) of the two structures were calculated. Note that theradial distribution function g(r) is a function representing theprobability density of atoms existing at a distance of r from one atom.As the correlation between atoms disappears, g(r) becomes closer to 1.

FIGS. 22A and 22B show final structures obtained by performing theclassical molecular dynamics calculation for 150 psec on the above twocalculation models. In addition, FIG. 23 shows the radial distributionfunction g (r) in each structure.

The model of single crystal shown in FIG. 22A is stable and keeps thecrystal structure even in the final structure, whereas the model of Sisubstitution shown in FIG. 22B is unstable, and it can be observed thatthe crystal structure is distorted with time and changes into anamorphous structure. When the radial distribution functions g(r) of thestructural models are compared with each other in FIG. 23, it is foundthat the single crystal model has peaks even at a long distance and hasa long-range order. On the other hand, it is found that in the model ofSi substitution, the peak disappears at a distance about 0.6 nm, and themodel of Si substitution does not have the long-range order.

The above calculation results indicate that when silicon (Si) isincluded in InGaZnO₄, InGaZnO₄ is likely to become amorphous. Further,according to the above results, even when InGaZnO₄ including silicon(Si) is heated at high temperature, such InGaZnO₄ is not crystallized.

Next, change in structure of the oxide semiconductor film 103 whencarbon atoms (C) are added was examined by classical molecular dynamicscalculation. The results thereof are described with reference to FIG.21A, FIGS. 24A and 24B, and FIG. 25. Note that simulation software“SCIGRESS ME” manufactured by Fujitsu Limited was used for classicalmolecular dynamics calculation.

Calculation models and calculation results are as follows. Note that inthis calculation, the Born-Mayer-Huggins potential was used. Further,for the interaction between carbon atoms (C), a Lennard-Jones potentialwas used.

A single crystal structure of InGaZnO₄ including 1680 atoms (see FIG.21A) and a structure of InGaZnO₄ including 1680 atoms in which 20 atomsof each of In, Ga, and Zn are substituted by carbon atoms (C) and 80atoms of oxygen (O) are substituted by carbon atoms (C) (see FIG. 24A)were formed as calculation models. In the model of C substitution shownin FIG. 24A, carbon atoms (C) are included at 8.33 at. %. Further, thedensity of the model of the single crystal shown in FIG. 21A is 6.36g/cm³, and the density of the model of C substitution shown in FIG. 24Ais 5.89 g/cm³.

At 1727° C. which is lower than the melting point of the InGaZnO₄ singlecrystal (about 2000° C. according to estimation by the classicalmolecular dynamics calculation), structure relaxation was performed onthe calculation models shown in FIG. 21A and FIG. 24A by the classicalmolecular dynamics calculation at a fixed pressure (1 atm) for 140 psec(time step width 0.2 fsec×750000 steps). The radial distributionfunctions g(r) of the two structures were calculated. Note that theradial distribution function g(r) is a function representing theprobability density of atoms existing at a distance of r from one atom.As the correlation between atoms disappears, g(r) becomes closer to 1.

FIG. 22A and FIG. 24B show final structures obtained by performing theclassical molecular dynamics calculation for 150 psec on the above twocalculation models. The radial distribution function g(r) in eachstructure is shown in FIG. 25.

The model of single crystal shown in FIG. 22A is stable and keeps thecrystal structure even in the final structure, whereas the model of Csubstitution shown in FIG. 24B is unstable, and it can be observed thatthe crystal structure is distorted with time and changes into anamorphous structure. As seen in FIG. 25, by comparing the radialdistribution functions g(r) of the structural models with each other, itis found that the model of single crystal has peaks even at a longdistance and the long-range order. On the other hand, it is found thatin the model of C substitution, the peak disappears at a distance about0.6 nm, and the model of C substitution does not have the long-rangeorder.

The above calculation results indicate that when carbon (C) is includedin InGaZnO₄, InGaZnO₄ is likely to become amorphous. In addition,according to the above results, even when InGaZnO₄ including carbon (C)is heated at high temperature, such InGaZnO₄ is not crystallized.

As described above, entry of impurities into the oxide semiconductorfilm causes a reduction in crystallinity of the oxide semiconductorfilm. Thus, in the semiconductor device shown in this embodiment, entryof impurities such as silicon into the oxide semiconductor film in thevicinity of the formed film surface is suppressed. As a result, in theoxide semiconductor film 103, a region in which a concentration ofsilicon distributed from an interface with the gate insulating film 102toward an inside of the oxide semiconductor film 103 is lower than orequal to 1.0 at. % is formed. Such a region is referred to as a region103 a. The concentration of silicon included in the region 103 a isfurther preferably lower than or equal to 0.1 at. %. Further, the region103 a is provided to be in contact with the gate insulating film 102 andhave a thickness less than or equal to 5 nm.

Note that a region in the oxide semiconductor film 103 other than theregion 103 a is referred to as a region 103 b. The concentration ofsilicon included in the region 103 b is lower than the concentration ofsilicon included in the region 103 a.

Further, in the case where impurities such as carbon is included in thegate insulating film 102, such impurities might also enter the oxidesemiconductor film 103 and serve as impurities, as in the case ofsilicon. In that case, the concentration of carbon included in theregion 103 a is lower than or equal to 1.0×10²⁰ atoms/cm³, preferablylower than or equal to 1.0×10¹⁹ atoms/cm³.

As described above, the concentration of impurities such as siliconentering the region 103 a in the oxide semiconductor film 103 isreduced, whereby change in characteristics of the transistor 110 can besuppressed. In addition, crystallization of the oxide semiconductor film103 can be progressed in the vicinity of the formed film surface.Further, in the case where the oxide semiconductor film 103 is a CAAC-OSfilm, a crystal portion can be formed even in the vicinity of the formedfilm surface. When transistors using such oxide semiconductor films aremanufactured, a semiconductor device with stable electriccharacteristics can be obtained.

Note that the details of the other components of the transistor aredescribed in description of a method for manufacturing the transistor110 below, with reference to FIGS. 4A to 4E.

Over the transistor 110, a planarity insulating film may be furtherformed. Further, openings may be formed in the gate insulating film 102,the protective insulating film 109, and the like in order that thesource electrode 105 a and the drain electrode 105 b may be electricallyconnected to a wiring. Furthermore, a second gate electrode may furtherbe provided above the oxide semiconductor film 103 to overlap with thegate electrode 101.

FIGS. 2A and 2B illustrate a transistor 120 having a different structurefrom that of the transistor 110 illustrated in FIGS. 1A and 1B. FIG. 2Ais a plan view, and FIG. 2B is a cross-sectional view taken along C-Dline in FIG. 2A. Note that part of components of the transistor 120(e.g., the protective insulating film 109 and the like) is notillustrated in FIG. 2A for brevity.

The transistor 120 illustrated in FIGS. 2A and 2B includes, over asubstrate 100 having an insulating surface, a gate electrode 101, a gateinsulating film 102 covering the gate electrode 101, an oxidesemiconductor film 103 provided to be in contact with the gateinsulating film 102 and overlap with at least the gate electrode 101, asource electrode 105 a and a drain electrode 105 b electricallyconnected to the oxide semiconductor film 103, and a protectiveinsulating film 109 covering the oxide semiconductor film 103 and thesource electrode 105 a and the drain electrode 105 b. A differencebetween the transistor 120 and the transistor 110 is that like the gateinsulating film 102, an insulating film including oxidized materialcontaining silicon is used as the protective insulating film 109 andthat a region 103 c is provided in the vicinity of an interface betweenthe oxide semiconductor film 103 and the protective insulating film 109.

The oxide semiconductor film 103 in the transistor 120 includes a region103 a, a region 103 b, and the region 103 c. The region 103 a in theoxide semiconductor film 103 is a region where a concentration ofsilicon distributed from the interface with the gate insulating film 102toward the inside of the oxide semiconductor film 103 is lower than orequal to 1.0 at. %. The region 103 a is preferably provided to be incontact with the gate insulating film 102 and have a thickness less thanor equal to 5 nm. The region 103 c in the oxide semiconductor film 103is a region where a concentration of silicon distributed from theinterface with the protective insulating film 109 toward the inside ofthe oxide semiconductor film 103 is lower than or equal to 1.0 at. %.The region 103 c is preferably provided to be in contact with theprotective insulating film 109 and have a thickness less than or equalto 5 nm. In the oxide semiconductor film 103, a region between theregion 103 a and the region 103 c is a region 103 b.

Note that the concentration of silicon included in the region 103 b islower than that of silicon included in the region 103 a. Theconcentration of silicon included in the region 103 a is furtherpreferably lower than or equal to 0.1 at. %.

Here, the concentration of silicon included in the region 103 a is lowerthan or equal to 1.0 at. %, preferably lower than or equal to 0.1 at. %,and the concentration of silicon included in the region 103 c is alsolower than or equal to 1.0 at. %, preferably lower than or equal to 0.1at. %. At this time, the concentration of silicon included in the region103 b is lower than the concentrations of silicon included in the region103 a and the region 103 c.

As described above, also in the region 103 c corresponding to a backchannel of the oxide semiconductor film 103, the concentration ofimpurities such as silicon is reduced, so that change in electriccharacteristics of the transistor 120 can be suppressed.

The other components are same as those of the semiconductor deviceillustrated in FIGS. 1A and 1B; thus, the description on FIGS. 1A and 1Bcan be referred to for the details.

Although the transistors illustrated in FIGS. 1A and 1B and FIGS. 2A and2B are so-called channel-etched type transistors, semiconductor devicesshown in this embodiment are not limited thereto. FIGS. 3A and 3Billustrate a channel-stop type transistor 130, which is different fromthe transistors illustrated in FIGS. 1A and 1B and FIGS. 2A and 2B. FIG.3A is a plan view, and FIG. 3B is a cross-sectional view taken alongline E-F in FIG. 3A. Note that part of components of the transistor 130(e.g., the protective insulating film 109 and the like) is notillustrated in FIG. 3A to avoid complexity. Further, in FIG. 3A, achannel protective film 108 is three-dimensionally illustrated for easyunderstanding.

The transistor 130 illustrated in FIGS. 3A and 3B includes, over asubstrate 100 having an insulating surface, a gate electrode 101, a gateinsulating film 102 covering the gate electrode 101, an oxidesemiconductor film 103 provided to be in contact with the gateinsulating film 102 and overlap with at least the gate electrode 101,the channel protective film 108 provided over and in contact with theoxide semiconductor film 103, a source electrode 105 a and a drainelectrode 105 b which are provided over the channel protective film 108and electrically connected to the oxide semiconductor film 103, and aprotective insulating film 109 covering the oxide semiconductor film 103and the source electrode 105 a and the drain electrode 105 b. Inaddition, as in the case of the transistor 110, the oxide semiconductorfilm 103 includes a region 103 a and a region 103 b. In other words, adifference from the transistor 110 is that the transistor 130 includesthe channel protective film 108.

As the channel protective film 108, an inorganic insulating filmcontaining oxygen is preferably used. For example, an insulating filmsuch as a silicon oxide film, a silicon oxynitirde film, an aluminumoxide film, an aluminum oxynitride film, a gallium oxide film, or ahafnium oxide film can be used. The preferable thickness of the channelprotective film 108 is greater than or equal to 5 nm and less than orequal to 300 nm.

The channel protective film 108 is provided over and in contact with theoxide semiconductor film 103 as described, whereby damage on the oxidesemiconductor film 103 on the back channel side, which is caused byetching the source electrode 105 a and the drain electrode 105 b (e.g.,damage caused by plasma or an etchant in etching treatment), can beprevented. Thus, the transistor 130 can obtain stable electriccharacteristics.

Further, as illustrated in FIG. 3B, an end portion of the channelprotective film 108 has a taper angle greater than or equal to 10° andless than or equal to 60°. The channel protective film 108 is formed tohave such a shape, whereby the electric field concentration in thevicinity of a lower end portion of the channel protective film 108 canbe relaxed.

The other components are the same as those in the semiconductor deviceillustrated in FIGS. 1A and 1B; thus, the description on FIGS. 1A and 1Bcan be referred to for the details.

<Example of Manufacturing Process of Transistor>

Examples of a manufacturing process of the transistor in FIGS. 1A and1B, FIGS. 2A and 2B, and FIGS. 3A and 3B will be described below withreference to FIGS. 4A to 4E and FIGS. 5A to 5E.

<Manufacturing Process of Transistor 110>

An example of a manufacturing process of the transistor 110 in FIGS. 1Aand 1B will be described with reference to FIGS. 4A to 4E.

First, the substrate 100 having an insulating surface is prepared. Thereis no particular limitation on a substrate that can be used as thesubstrate 100 having an insulating surface as long as it has at leastheat resistance to withstand heat treatment performed later. Forexample, a glass substrate of barium borosilicate glass,aluminoborosilicate glass, or the like, a ceramic substrate, a quartzsubstrate, or a sapphire substrate can be used. As long as the substrate100 has an insulating surface, a single crystal semiconductor substrateor a polycrystalline semiconductor substrate of silicon, siliconcarbide, or the like; a compound semiconductor substrate of silicongermanium or the like; an SOI substrate; or the like can be used.

A flexible substrate may alternatively be used as the substrate 100.When a flexible substrate is used, a transistor including the oxidesemiconductor film 103 may be directly formed over the flexiblesubstrate. Alternatively, a transistor including the oxide semiconductorfilm 103 may be formed over a manufacturing substrate, and then, thetransistor may be separated and transferred to a flexible substrate.Note that in order to separate the transistor from the manufacturingsubstrate and transfer it to the flexible substrate, a separation layermay be provided between the manufacturing substrate and the transistorincluding the oxide semiconductor film 103.

An insulating film functioning as a base film may be provided betweenthe substrate 100 and the gate electrode 101. The base film has afunction of preventing diffusion of impurities such as hydrogen ormoisture from the substrate 100, and can be formed to have a singlelayer or stacked structure using one or more films selected from asilicon nitride film, a silicon oxide film, a silicon nitride oxidefilm, and a silicon oxynitride film.

Next, a conductive film used for formation of a gate electrode (as wellas a wiring formed in the same layer as the gate electrode) is formedover the substrate 100. The conductive film used for the gate electrodecan be formed using, for example, a metal material such as molybdenum,titanium, tantalum, tungsten, aluminum, copper, neodymium, or scandium,or an alloy material including any of these materials as a maincomponent. Alternatively, the conductive film used for the gateelectrode may be formed using a conductive metal oxide. As theconductive metal oxide, indium oxide (In₂O₃), tin oxide (SnO₂), zincoxide (ZnO), indium tin oxide (In₂O₃—SnO₂, which is abbreviated to ITOin some cases), indium zinc oxide (In₂O₃—ZnO), or any of these metaloxide materials in which silicon or silicon oxide is included can beused. The gate electrode can be formed to have a single layer or astacked structure using any of the above materials. There is noparticular limitation on the method for forming the conductive film, anda variety of film formation methods such as an evaporation method, a CVDmethod, a sputtering method, or a spin coating method can be employed.

Next, a resist mask is formed over the conductive film through aphotolithography step and selective etching is performed, so that thegate electrode 101 is formed. Then, the resist mask is removed. Theresist mask used for forming the gate electrode 101 may be formed by aninkjet method. Formation of the resist mask by an inkjet method needs nophotomask; thus, manufacturing cost can be reduced. For etching the gateelectrode 101, wet etching, dry etching, or both of them may beemployed.

Next, the gate insulating film 102 is formed to cover the gate electrode101 (see FIG. 4A). The gate insulating film 102 can have a thicknessgreater than or equal to 1 nm and less than or equal to 500 nm, forexample. There is no particular limitation on the method for forming thegate insulating film 102; for example, a sputtering method, an MBEmethod, a CVD method, a pulse laser deposition method, an ALD method, orthe like can be used as appropriate for formation of the gate insulatingfilm 102.

For the gate insulating layer 102, an oxide insulating film having asufficient withstand voltage and a sufficient insulating property ispreferably used. In the case where the gate insulating film 102 has asingle-layer structure, an insulating film including oxidized materialcontaining silicon, such as a silicon oxide film, may be used.

Alternatively, the gate insulating film 102 may have a stackedstructure. In the case where the gate insulating film 102 has a stackedstructure, silicon oxide may be stacked over gallium oxide, aluminumoxide, silicon nitride, silicon oxynitride, aluminum oxynitride, yttriumoxide, lanthanum oxide, silicon nitride oxide, or the like.Alternatively, silicon oxide may be stacked over a high-k material suchas hafnium oxide, hafnium silicate (HfSi_(x)O_(y) (x>0, y>0)), hafniumsilicate to which nitrogen is added (HfSiO_(x)N_(y) (x>0, y>0)), orhafnium aluminate (HfAl_(x)O_(y) (x>0, y>0)). The use of such a high-kmaterial enables a reduction in gate leakage current.

When an oxide insulating film is used as the gate insulating film 102,part of oxygen contained in the oxide insulating film can be released byperforming heat treatment described later; thus, oxygen can be suppliedto the oxide semiconductor film 103, and oxygen vacancies in the oxidesemiconductor film 103 can be filled. In particular, the gate insulatingfilm 102 preferably contains a large amount of oxygen which exceeds atleast the stoichiometry in (a bulk of) the gate insulating film 102. Forexample, a film of silicon oxide represented by the formula SiO_(2+α)(α>0) is preferably used as the gate insulating film 102. When such asilicon oxide film is used as the gate insulating film 102, oxygen canbe supplied to the oxide semiconductor film 103, so that the transistor110 using the oxide semiconductor film 103 can have favorable transistorcharacteristics.

Further, before the oxide semiconductor film 103 is formed,planarization treatment may be performed on the gate insulating film102. Although not particularly limited, the planarization treatment canbe dry etching, plasma treatment, polishing (e.g., chemical mechanicalpolishing (CMP)), or the like.

As plasma treatment, reverse sputtering in which an argon gas isintroduced and plasma is generated can be performed. The reversesputtering is a method in which voltage is applied to a substrate sidewith use of an RF power source in an argon atmosphere and plasma isgenerated in the vicinity of the substrate so that a surface ismodified. Note that instead of an argon atmosphere, a nitrogenatmosphere, a helium atmosphere, an oxygen atmosphere, or the like maybe used. The reverse sputtering can remove particle substances (alsoreferred to as particles or dust) attached to a surface where the oxidesemiconductor film 103 is formed.

As the planarization treatment, polishing treatment, dry-etchingtreatment, or plasma treatment may be performed plural times and/or incombination. In the case where the treatments are combined, the order ofsteps is not particularly limited and may be set as appropriate inaccordance with roughness of the surface where the oxide semiconductorfilm 103 is formed.

Further, in order that hydrogen or water may be contained in the oxidesemiconductor film 103 as little as possible in a formation step of theoxide semiconductor film 103, it is preferable that the substrate 100 onwhich the gate insulating film 102 is already formed be preheated in apreheating chamber of a sputtering apparatus as pretreatment forformation of the oxide semiconductor film 103 so that impurities such ashydrogen and moisture adsorbed to the substrate 100 and the gateinsulating film 102 are removed and evacuated. As an evacuation unitprovided in the preheating chamber, a cryopump is preferable.

Next, over the gate insulating film 102, the oxide semiconductor film103 having a thickness greater than 5 nm and less than or equal to 200nm, preferably greater than or equal to 10 nm and less than or equal to30 nm is formed (see FIG. 4B). The oxide semiconductor film 103preferably has a structure with crystallinity of single crystal ormicrocrystal. Further, the oxide semiconductor film 103 is preferably aCAAC-OS film. Note that it is preferable that the gate insulating film102 and the oxide semiconductor film 103 be formed successively withoutbeing exposed to air.

In this embodiment, as the oxide semiconductor film 103, an oxidesemiconductor film is formed using an In—Ga—Zn-based oxide target by asputtering method. Alternatively, the oxide semiconductor film 103 canbe formed by a sputtering method in a rare gas (typically, argon)atmosphere, an oxygen atmosphere, or a mixed atmosphere of a rare gasand oxygen.

As a target used for forming an In—Ga—Zn—O film as the oxidesemiconductor film 103 by a sputtering method, for example, an oxidetarget with an atomic ratio where In:Ga:Zn=1:1:1, an oxide target withan atomic ratio where In:Ga:Zn=3:1:2, or an oxide target with an atomicratio where In:Ga:Zn=2:1:3 can be used. However, a material andcomposition of a target used for formation of the oxide semiconductorfilm 103 is not limited to the above.

The relative density of the oxide target is higher than or equal to 90%and lower than or equal to 100%, preferably higher than or equal to 95%and lower than or equal to 99.9%. By using the oxide target with highrelative density, the oxide semiconductor film 103 can be a dense film.

It is preferable that a high-purity gas from which impurities such ashydrogen, water, a hydroxyl group, or a hydride is removed be used asthe sputtering gas for the formation of the oxide semiconductor film103.

There are three heating methods for forming a CAAC-OS film when theCAAC-OS film is used as the oxide semiconductor film 103. One of themethods (first method) is to form an oxide semiconductor film at atemperature higher than or equal to 200° C. and lower than or equal to450° C. to form, in the oxide semiconductor film, crystal portions inwhich the c-axes are aligned in the direction perpendicular to a surfacewhere the oxide semiconductor film is formed or a surface of the oxidesemiconductor film. Another method (second method) is to form an oxidesemiconductor film with a small thickness and then heat it at atemperature higher than or equal to 200° C. and lower than or equal to700° C., to form, in the oxide semiconductor film, crystal portions inwhich the c-axes are aligned in the direction perpendicular to a surfacewhere the oxide semiconductor film is formed or a surface of the oxidesemiconductor film. The other method (third method) is to form a firstoxide semiconductor film with a small thickness, then heat it at atemperature higher than or equal to 200° C. and lower than or equal to700° C., and form a second oxide semiconductor film, to form, in theoxide semiconductor film, crystal portions in which the c-axes arealigned in the direction perpendicular to a surface where the oxidesemiconductor film is formed or a surface of the oxide semiconductorfilm.

By heating the substrate 100 during film formation, the concentration ofimpurities such as hydrogen or water in the oxide semiconductor film 103can be reduced. In addition, damage by sputtering can be reduced, whichis preferable.

Note that when an oxide semiconductor film having crystallinity (singlecrystal or microcrystal) different from the CAAC-OS film is formed asthe oxide semiconductor film 103, the film formation temperature is notparticularly limited.

In the case where a CAAC-OS film is used as the oxide semiconductor film103, for example, the CAAC-OS film is deposited by a sputtering methodwith a polycrystalline oxide semiconductor sputtering target. When ionscollide with the sputtering target, a crystal region included in thesputtering target may be separated from the target along an a-b plane;in other words, a sputtered particle having a plane parallel to an a-bplane (flat-plate-like sputtered particle or pellet-like sputteredparticle) may flake off from the sputtering target. In that case, theflat-plate-like sputtered particle reaches a substrate while keepingtheir crystal state, whereby the CAAC-OS film can be formed.

For the deposition of the CAAC-OS film, the following conditions arepreferably used.

By reducing the amount of impurities entering the CAAC-OS film duringthe deposition, the crystal state can be prevented from being broken bythe impurities. For example, the concentration of impurities (e.g.,hydrogen, water, carbon dioxide, or nitrogen) which exist in thedeposition chamber may be reduced. Furthermore, the concentration ofimpurities in a deposition gas may be reduced. Specifically, adeposition gas whose dew point is −80° C. or lower, preferably −100° C.or lower is used.

By increasing the substrate heating temperature during the deposition,migration of a sputtered particle is likely to occur after the sputteredparticle reaches a substrate surface. Specifically, the substrateheating temperature during the deposition is higher than or equal to100° C. and lower than or equal to 740° C., preferably higher than orequal to 200° C. and lower than or equal to 500° C. By increasing thesubstrate heating temperature during the deposition, when theflat-plate-like sputtered particle reaches the substrate, migrationoccurs on the substrate surface, so that a flat plane of theflat-plate-like sputtered particle is attached to the substrate.

Furthermore, it is preferable that the proportion of oxygen in thedeposition gas be increased and the power be optimized in order toreduce plasma damage at the deposition. The proportion of oxygen in thedeposition gas is 30 vol. % or higher, preferably 100 vol. %.

As an example of the sputtering target, a polycrystalline In—Ga—Zn-basedoxide target is described below.

The In—Ga—Zn-based oxide target, which is polycrystalline, is made bymixing InO_(X) powder, GaO_(Y) powder, and ZnO_(Z) powder in apredetermined molar ratio, applying pressure, and performing heattreatment at a temperature higher than or equal to 1000° C. and lowerthan or equal to 1500° C. Note that X, Y, and Z are each a givenpositive number. Here, the predetermined molar ratio of InO_(X) powderto GaO_(Y) powder and ZnO_(Z) powder is, for example, 2:2:1, 8:4:3,3:1:1, 1:1:1, 4:2:3, or 3:1:2. The kinds of powder and the molar ratiofor mixing powder may be determined as appropriate depending on thedesired sputtering target.

Then, a sputtering gas from which hydrogen and moisture have beenremoved is introduced into the deposition chamber while moistureremaining therein is removed, and the oxide semiconductor film 103 isdeposited over the substrate 100 with the use of the above target. Inorder to remove moisture remaining in the deposition chamber, anentrapment vacuum pump such as a cryopump, an ion pump, or a titaniumsublimation pump is preferably used. Further, an evacuation unit may bea turbo pump provided with a cold trap. From the deposition chamberwhich is evacuated with a cryopump, a hydrogen atom, a compoundcontaining a hydrogen atom such as water (H₂O) (more preferably, also acompound containing a carbon atom), and the like are removed, wherebythe concentration of impurities such as hydrogen or moisture in theoxide semiconductor film 103 formed in the deposition chamber can bereduced.

Note that in the case where the oxide semiconductor film 103 is formedby a sputtering method, when a particle for forming the oxidesemiconductor film 103 collides with the gate insulating film 102, anelement that is a constituent element of the gate insulating film 102enters the oxide semiconductor film 103 (this phenomenon is calledmixing or mixing effect). Such a mixing phenomenon significantly occursin the oxide semiconductor film 103 in the vicinity of the interfacewith the gate insulating film 102, specifically occurs in theabove-described region 103 a. Since in the transistor described in thisembodiment, a channel region is formed in the oxide semiconductor film103 in the vicinity of the gate insulating film 102, a constituentelement of the gate insulating film 102, which enters the region andserves as an impurity therein, may be a cause of a reduction in on-statecharacteristics (e.g., on-state current) of the transistor.

The possibility of mixing occurring in the vicinity of an interfacebetween the gate insulating film 102 and the oxide semiconductor film103 when the oxide semiconductor film 103 is formed over the gateinsulating film 102 was examined by classical molecular dynamicscalculation. Here, the results thereof are described. Note thatsimulation software “SCIGRESS ME” manufactured by Fujitsu Limited wasused for the calculation.

A model shown in FIG. 6 was formed using an amorphous silicon oxide(hereinafter, referred to as a-SiO₂) film as a gate insulating film. Thesize of a unit cell (a calculation unit cell) used in calculation is setto be 3 nm in the x-axis direction, 3 nm in the y-axis direction, and7.5 nm in the z-axis direction. The x-axis and the y-axis refer to thedirections parallel to the a-SiO₂ film, and the z-axis refers to thethickness direction of the a-SiO₂ film. Note that in the calculation,the periodic boundary condition is applied in the x-axis direction andthe y-axis direction so that a film which is sufficiently large in thex-axis direction and the y-axis direction can be assumed.

Next, indium atoms, gallium atoms, zinc atoms, and oxygen atoms whoseratio is 1:1:1:4 (the total number of atoms is 840) were ejected fromthe upper portion (in FIG. 6, an atom-generation portion) over thea-SiO₂ film toward the lower portion, and classical molecular dynamicscalculation was performed at a temperature of 300° C. for 2 nsec (thetime step: 0.2 fs, the number of steps: ten million). Note that one atomhas an energy of 1 eV.

FIGS. 7A to 7C and FIGS. 8A to 8C show the calculation results. FIG. 7Ashows arrangement of oxygen atoms and silicon atoms at 0 sec; FIG. 7Bshows arrangement of oxygen atoms, silicon atoms, gallium atoms, andzinc atoms after 1 nsec; and FIG. 7C shows arrangement of oxygen atoms,silicon atoms, gallium atoms, and zinc atoms after 2 nsec. FIG. 8A showsarrangement of oxygen atoms, silicon atoms, gallium atoms, and zincatoms after 2 nsec; FIG. 8B shows arrangement of only silicon atomsafter 2 nsec; and FIG. 8C shows arrangement of indium atoms, galliumatoms, and zinc atoms after 2 nsec.

By comparing the arrangement of only silicon atoms shown in FIG. 8B andthe arrangement of indium atoms, gallium atoms, and zinc atoms shown inFIG. 8C, it was confirmed that the indium atoms, the gallium atoms, andthe zinc atoms entered a layer of silicon atoms.

The above calculation results indicate that by injecting indium atoms,gallium atoms, zinc atoms, and oxygen atoms into the a-SiO₂ film, alayer in which silicon atoms, indium atoms, gallium atoms, zinc atoms,and oxygen atoms are mixed is formed between the a-SiO₂ film and an IGZOfilm. Note that one atom has an energy of 1 eV.

According to the above results, in order to prevent formation of a layerin which the oxide semiconductor film 103 and the gate insulating film102 are mixed, it is effective to reduce an impact caused by collisionof a particle for forming the oxide semiconductor film 103 with the gateinsulating film 102. For achieving the above, a method in which thepower for deposition of the oxide semiconductor film 103 is low or amethod in which the pressure for deposition thereof is high can be used,for example. Alternatively, a distance between a target and a substrateover which the film is deposited (hereinafter, referred to as a T-Sdistance) may be increased.

Note that mixing caused by sputtering is likely to be generated in theoxide semiconductor film 103 in the vicinity of the interface with thegate insulating film 102 as described above. Thus, part of the oxidesemiconductor film in the vicinity of the interface is deposited bysputtering under the condition that the impact caused by a particle forforming the oxide semiconductor film 103, which collides with the gateinsulating film 102 is low, and accordingly the mixing effect isreduced; after that, in performing the rest of deposition, the impact ofcollision may be increased. For example, part of the oxide semiconductorfilm 103 in the vicinity of the interface may be deposited under thecondition that the power for depositing the oxide semiconductor film 103is low, and then, deposition of the oxide semiconductor film may becarried on under the condition that the deposition power is increased.Alternatively, part of the oxide semiconductor film 103 in the vicinityof the interface may be deposited under the condition that the pressurefor depositing the oxide semiconductor film 103 is high, and then,deposition of the oxide semiconductor film may be carried on under thecondition that the deposition pressure is reduced. Furtheralternatively, part of the oxide semiconductor film 103 in the vicinityof the interface may be deposited under the condition that the T-Sdistance is large, and then, deposition of the oxide semiconductor filmmay be carried on under the condition that the T-S distance isdecreased.

The specific value of the deposition power is 5 kW or lower, preferably,1 kW or lower, further preferably 500 W or lower, furthermorepreferably, 200 W or lower. However, as the deposition power is reduced,the deposition rate of the oxide semiconductor film 103 is decreased.Further, in the case where the deposition power is significantly low,plasma is less likely to be generated in a sputtering apparatus, and thepossibility that normal deposition treatment cannot be performed isincreased. Thus, it is preferable that the deposition power be 5% (orhigher) of the maximum power that can be applied in the sputteringapparatus. In considering a reduction in the deposition power, apractitioner may select the optimum power value as appropriate in termsof performance of the sputtering apparatus or the thickness of the oxidesemiconductor film 103 so that deposition can be normally performed, aslong as the manufacturing process of the transistor 110 (cycle time) isnot significantly affected by the deposition time.

The specific value of the deposition pressure is 0.4 Pa or higher,preferably, 1.0 Pa or higher, further preferably 2.0 Pa or higher,furthermore preferably, 5.0 Pa or higher. However, as the depositionpressure is increased, quality of a film that is to be deposited tendsto deteriorate (e.g., the film quality is sparse). Thus, it ispreferable that the deposition pressure is 100 Pa or lower. Inconsidering an increase in the deposition pressure, a practitioner mayselect the optimum pressure value as appropriate in terms ofcharacteristics necessary for the oxide semiconductor film 103 (e.g.,field-effect mobility or the like).

The specific value of the T-S distance is 30 mm or more, preferably 50mm or more, further preferably 100 mm or more, furthermore preferably300 mm or more. Note that as the T-S distance is extremely increased,the deposition rate of the oxide semiconductor film 103 is decreased.Thus, it is preferable that the T-S distance be 500 mm or less. Inconsidering an increase in the T-S distance, a practitioner may selectthe optimum T-S distance as appropriate as long as the manufacturingprocess of the transistor 110 (cycle time) is not significantly affectedby the deposition time.

Note that in order to reduce the impact of a particle for forming theoxide semiconductor film 103, which collides with the gate insulatingfilm 102, the oxide semiconductor film 103 may be deposited in a statewhere one or more of the conditions of deposition power, depositionpressure, and T-S distance are set in the above range.

In the case where as the sputtering apparatus, a magnetron-typesputtering apparatus in which a target and a substrate over which a filmis to be deposited are set in substantially parallel to each other(simply the apparatus is also called a magnetron sputtering apparatus)is used, besides a particle for forming the oxide semiconductor film103, plasma, a secondary electron, or the like collides with the gateinsulating film 102; thus, an element included in the gate insulatingfilm 102 is more likely to enter the oxide semiconductor film 103.Therefore, as a sputtering apparatus used for depositing the oxidesemiconductor film 103, a facing-target-type sputtering apparatus (alsocalled mirrortron sputtering apparatus) may be used. In the apparatus,two targets are set to face each other, a substrate over which a film isto be deposited is set in a portion other than a space sandwichedbetween the two targets to be in a direction substantially perpendicularto the targets. Then, high-density plasma is generated between the twotargets facing each other, and surfaces of the targets (which are usedfor deposition of the oxide semiconductor film 103) are sputtered by theplasma, whereby the oxide semiconductor film 103 is deposited over thesubstrate. Thus, the substrate where a film is to be deposited is not(or hardly) exposed to plasma or a secondary electron directly.

Further, in the case where the oxide semiconductor film 103 is depositedby sputtering in a rare gas atmosphere, helium may be used instead ofargon. When helium whose atomic weight is smaller than that of argon isused, the impact of a particle for forming the oxide semiconductor film103, which collides with the gate insulating film 102, can be reduced.Furthermore, after part of the oxide semiconductor film 103 in thevicinity of the interface with the gate insulating film 102 is depositedin a helium atmosphere, the atmosphere in the deposition chamber isswitched into an argon atmosphere, whereby the deposition rate of theoxide semiconductor film 103 can be increased.

Alternatively, the oxide semiconductor film 103 may be deposited by amethod by which the impact on the gate insulating film 102 is small,such as an atomic layer deposition (ALD) method, an evaporation method,or a coating method.

As described above, the oxide semiconductor film 103 is deposited underthe condition that the impact of a particle for forming the oxidesemiconductor film 103, which collides with the gate insulating film 102is reduced, so that in the oxide semiconductor film 103, the region 103a where a concentration of silicon distributed from an interface withthe gate insulating film 102 toward the inside of the oxidesemiconductor film 103 is lower than or equal to 1.0 at. % and theregion 103 b where silicon is lower than that in the region 103 a areformed. Here, the region 103 b indicates a region in the oxidesemiconductor film 103 other than the region 103 a. Further, theconcentration of silicon included in the region 103 a is preferablylower than or equal to 0.1 at. %.

Further, when the oxide semiconductor film 103 is deposited in such amanner, entry of impurities such as carbon included in the gateinsulating film 102 into the oxide semiconductor film 103 can be alsoreduced. Thus, the concentration of carbon included in the region 103 ais lower than or equal to 1.0×10²⁰ atoms/cm³, preferably lower than orequal to 1.0×10¹⁹ atoms/cm³.

In the case where a CAAC-OS film is formed as the oxide semiconductorfilm 103 while being heated (the first method), the amount of impuritiessuch as silicon entering the region 103 a is reduced, so that a crystalportion in which a c-axis is aligned in a direction perpendicular to aformed film surface or a surface of the oxide semiconductor film can beformed even in the vicinity of the formed film surface of the CAAC-OSfilm.

Further, when the oxide semiconductor film 103 is deposited under theconduction that the impact of a particle for forming the oxidesemiconductor film 103, which collides with the gate insulating film 102is reduced, entry of the constituent element of the oxide semiconductorfilm 103 into the gate insulating film 102 can be suppressed. Thus,entry of the constituent element having high conductivity, such as ametal element, of the oxide semiconductor film 103 into the gateinsulating film 102 can be suppressed, and accordingly, a reduction inresistivity of the gate insulating film 102 can be prevented.

After the oxide semiconductor film 103 is deposited, heat treatment maybe performed on the oxide semiconductor film 103. The temperature of theheat treatment is higher than or equal to 200° C. and lower than orequal to 700° C., or lower than the strain point of the substrate. Whenthe heat treatment is performed, excess hydrogen (including water and ahydroxyl group) can be removed.

In the case where a CAAC-OS film is formed by the second or thirdmethod, the above heat treatment is performed, so that a crystal portionin which a c-axis is aligned in a direction perpendicular to a formedfilm surface or a surface of the oxide semiconductor film can be formed.In addition, the concentration of impurities such as silicon is reducedin the region 103 a in the oxide semiconductor film 103; thus, thecrystal portion can be formed even in the vicinity of the formed filmsurface of the oxide semiconductor film 103.

The heat treatment can be performed in such a manner that, for example,an object to be processed is introduced into an electric furnace inwhich a resistance heater or the like is used and heated at 450° C. in anitrogen atmosphere for one hour. During the heat treatment, the oxidesemiconductor film 103 is not exposed to air to prevent entry of waterand hydrogen.

The heat treatment apparatus is not limited to the electric furnace andmay be an apparatus for heating an object by thermal radiation orthermal conduction from a medium such as a heated gas. For example, arapid thermal anneal (RTA) apparatus such as a gas rapid thermal anneal(GRTA) apparatus or a lamp rapid thermal anneal (LRTA) apparatus can beused. An LRTA apparatus is an apparatus for heating an object to beprocessed by radiation of light (an electromagnetic wave) emitted from alamp such as a halogen lamp, a metal halide lamp, a xenon arc lamp, acarbon arc lamp, a high pressure sodium lamp, or a high pressure mercurylamp. A GRTA apparatus is an apparatus for performing heat treatmentusing a high-temperature gas. As the gas, an inert gas which does notreact with an object to be processed by heat treatment, such as nitrogenor a rare gas such as argon is used.

For example, as the heat treatment, the GRTA process may be performed asfollows. The object is put in a heated inert gas atmosphere, heated forseveral minutes, and taken out of the inert gas atmosphere. The GRTAprocess enables high-temperature heat treatment for a short time.Moreover, the GRTA process can be employed even when the temperatureexceeds the upper temperature limit of the object. Note that the inertgas may be switched to a gas containing oxygen during the process.

Note that as the inert gas atmosphere, an atmosphere that containsnitrogen or a rare gas (e.g., helium, neon, or argon) as its maincomponent and does not contain water, hydrogen, or the like ispreferably used. For example, the purity of nitrogen or a rare gas suchas helium, neon, or argon introduced into a heat treatment apparatus isgreater than or equal to 6N (99.9999%), preferably greater than or equalto 7N (99.99999%) (that is, the concentration of the impurities is lessthan or equal to 1 ppm, preferably less than or equal to 0.1 ppm).

In addition, after the oxide semiconductor film 103 is heated by theheat treatment, a high-purity oxygen gas, a dinitrogen monoxide gas, ahigh-purity dinitrogen monoxide gas, or ultra dry air (the moistureamount is less than or equal to 20 ppm (−55° C. by conversion into a dewpoint), preferably less than or equal to 1 ppm, or further preferablyless than or equal to 10 ppb, in the case where measurement is performedwith use of a dew point meter of a cavity ring down laser spectroscopy(CRDS) system) may be introduced into the same furnace. It is preferablethat water, hydrogen, or the like be not contained in the oxygen gas orthe dinitrogen monoxide gas. Alternatively, the purity of the oxygen gasor the dinitrogen monoxide gas which is introduced into the heattreatment apparatus is preferably greater than or equal to 6N, furtherpreferably greater than or equal to 7N (i.e., the impurity concentrationin the oxygen gas or the dinitrogen monoxide gas is preferably less thanor equal to 1 ppm, further preferably less than or equal to 0.1 ppm). Bythe effect of the oxygen gas or the dinitrogen monoxide gas, oxygenwhich is a main component of the oxide semiconductor and which has beenreduced at the same time as the heat treatment is supplied, so that theoxide semiconductor film can be a high-purity and electrically i-type(intrinsic) oxide semiconductor film.

In the case where a CAAC-OS film is formed by the third method, an oxidesemiconductor film may be additionally formed. Thus, the additionallyformed oxide semiconductor film can also have a crystal portion with useof the crystal portion as a seed in which a c-axis is aligned in adirection perpendicular to the formed film surface or the surface of theoxide semiconductor film.

Note that in the case where an oxide semiconductor film havingcrystallinity (single crystal or microcrystalline) different from aCAAC-OS film is formed, by performing the heat treatment, the oxidesemiconductor film can be crystallized. In addition, since theconcentration of impurities such as silicon is reduced in the region 103a in the oxide semiconductor film 103, the oxide semiconductor film evenin the vicinity of the formed film surface can be crystallized.

Note that the case is described here in which before the oxidesemiconductor film is processed to have an island shape, the heattreatment is performed; however, one embodiment of the disclosedinvention is not construed as being limited thereto. The heat treatmentmay be performed after the oxide semiconductor film is processed to havean island shape.

Next, the oxide semiconductor film 103 is preferably processed into theisland-shape oxide semiconductor film 103 by a photolithography step(see FIG. 4C). A resist mask which is used in the formation of theisland-shaped oxide semiconductor film 103 may be formed by an ink-jetmethod. Formation of the resist mask by an inkjet method needs nophotomask; thus, manufacturing cost can be reduced. Note that etching ofthe oxide semiconductor film 103 may be dry etching, wet etching, orboth dry etching and wet etching.

Here, as illustrated in FIG. 4C, an end portion of the oxidesemiconductor film 103 preferably has a taper angle of 20° to 50°. Whenthe oxide semiconductor film 103 has a perpendicular end portion, oxygenis easily released from the oxide semiconductor film 103. When the oxidesemiconductor film 103 has a tapered end portion, generation of oxygenvacancies is suppressed, and thus generation of leakage current of thetransistor 110 can be reduced.

Next, a conductive film used for a source electrode and a drainelectrode (as well as a wiring formed in the same layer as the gateelectrode) is formed over the oxide semiconductor film 103. As theconductive film used for the source electrode and the drain electrode,for example, a metal film containing an element selected from aluminum,chromium, copper, tantalum, titanium, molybdenum, or tungsten, or ametal nitride film containing any of the above elements as its component(e.g., a titanium nitride film, a molybdenum nitride film, or a tungstennitride film) can be used. Alternatively, the conductive film may have astructure in which a film of a high-melting-point metal such astitanium, molybdenum, or tungsten, or a nitride film of any of thesemetals (a titanium nitride film, a molybdenum nitride film, or atungsten nitride film) is stacked on either or both of the bottomsurface and the top surface of a metal film of aluminum, copper, or thelike. Further, the conductive film used for the source electrode and thedrain electrode may be formed using a conductive metal oxide. As theconductive metal oxide, indium oxide (In₂O₃), tin oxide (SnO₂), zincoxide (ZnO), indium tin oxide (In₂O₃—SnO₂, which is abbreviated to ITOin some cases), or indium zinc oxide (In₂O₃—ZnO) can be used. Theconductive film used for the source electrode and the drain electrodecan be formed using any of the above materials to have a single layer ora stacked structure. There is no particular limitation on the method forforming the conductive film, and a variety of film formation methodssuch as an evaporation method, a CVD method, a sputtering method, or aspin coating method can be employed.

A resist mask is formed over the conductive film by a photolithographystep, selective etching is performed so that the source electrode 105 aand the drain electrode 105 b are formed, and after that, the resistmask is removed (see FIG. 4D). For the light exposure for forming theresist mask in the photolithography step, ultraviolet, KrF laser, or ArFlaser is preferably used. In this step, a channel length L of atransistor that is to be completed in a later step is determined by adistance between a lower end of the source electrode 105 a and a lowerend of the drain electrode 105 b that are adjacent to each other overthe oxide semiconductor film 103. When light exposure is performed for achannel length L smaller than 25 nm, the light exposure for forming theresist mask in the photolithography step may be performed using extremeultraviolet light having an extremely short wavelength of severalnanometers to several tens of nanometers, for example. In the lightexposure by extreme ultraviolet light, the resolution is high and thefocus depth is large. Thus, the channel length L of the transistorformed later can be reduced, whereby the operation speed of a circuitcan be increased.

In order to reduce the number of photomasks used in a photolithographystep and reduce the number of photolithography steps, an etching stepmay be performed with use of a multi-tone mask which is a light-exposuremask through which light is transmitted to have a plurality ofintensities. A resist mask formed with use of a multi-tone mask has aplurality of thicknesses and further can be changed in shape by etching;therefore, the resist mask can be used in a plurality of etching stepsfor processing into different patterns. Therefore, a resist maskcorresponding to at least two kinds or more of different patterns can beformed by one multi-tone mask. Thus, the number of light-exposure maskscan be reduced and the number of corresponding photolithography stepscan be also reduced, whereby simplification of a process can beachieved.

Note that it is preferable that etching conditions be optimized so asnot to etch and divide the oxide semiconductor film 103 when theconductive film is etched. However, it is difficult to obtain etchingconditions in which only the conductive film is etched and the oxidesemiconductor film 103 is not etched at all. In some cases, only part ofthe oxide semiconductor film 103, e.g., 5% to 50% in thickness of theoxide semiconductor film 103, is etched, so that the oxide semiconductorfilm 103 has a groove portion (a recessed portion) when the conductivefilm is etched.

Next, the protective insulating film 109 which covers the sourceelectrode 105 a and the drain electrode 105 b and is in contact withpart of the oxide semiconductor film 103 is formed (see FIG. 4E). Theprotective insulating film 109 may be formed using an inorganicinsulating film as a single layer or a stacked layer of any of oxideinsulating films such as a silicon oxide film, a silicon oxynitridefilm, an aluminum oxide film, an aluminum oxynitride film, a galliumoxide film, and a hafnium oxide film. Further, over the above oxideinsulating film, a single layer or a stacked layer of any of nitrideinsulating films such as a silicon nitride film, a silicon nitride oxidefilm, an aluminum nitride film, and an aluminum nitride oxide film maybe formed. For example, a silicon oxide film and an aluminum oxide filmare sequentially formed to be stacked on the source electrode 105 a andthe drain electrode 105 b side by a sputtering method.

Note that in this step, in the case where the protective insulating film109 is formed by a sputtering method, it is effective to reduce theimpact of a particle for forming the protective insulating film 109,which collides with the oxide semiconductor film 103, as like formationof the oxide semiconductor film 103. Thus, the region 103 c is formed inthe vicinity of the interface between the oxide semiconductor film 103and the protective insulating film 109. Through this step, thetransistor 120 illustrated in FIGS. 2A and 2B can be obtained. Theregion 103 c in the oxide semiconductor film 103 is a region where aconcentration of silicon distributed from an interface with theprotective insulating film 109 toward the inside of the oxidesemiconductor film 103 is lower than or equal to 1.0 at. %. The region103 c is preferably provided to be in contact with the protectiveinsulating film 109 and have a thickness less than or equal to 5 nm.

Here, as the protective insulating film 109, an insulating film similarto the gate insulating film 102 can be used. In order to preventimpurities such as silicon from entering the oxide semiconductor film103, mixing may be suppressed in the vicinity of the interface betweenthe oxide semiconductor film 103 and the protective insulating film 109;thus, the impact of silicon included in the protective insulating film109 colliding with the oxide semiconductor film 103 may be reduced. Forexample, as an applicable method, the power for depositing theprotective insulating film 109 is reduced, the pressure for depositingthe protective insulating film 109 is increased, or the T-S distance isincreased.

As described above, the concentration of impurities such as silicon canalso be reduced in the region 103 c corresponding to the back channel ofthe oxide semiconductor film 103.

After the above steps, the manufacturing method of the transistor 110and that of the transistor 120 are similar to each other.

After the protective insulating film 109 is formed, heat treatment ispreferably performed on the oxide semiconductor film 103. Thetemperature of the heat treatment is higher than or equal to 300° C. andlower than or equal to 700° C., or lower than the strain point of thesubstrate.

The heat treatment may be performed in an atmosphere of nitrogen,oxygen, ultra-dry air (the moisture content is less than or equal to 20ppm, preferably less than or equal to 1 ppm, further preferably lessthan or equal to 10 ppb), or a rare gas (such as argon or helium). Notethat it is preferable that water, hydrogen, and the like be notcontained in the atmosphere of nitrogen, oxygen, ultra-dry air, a raregas, or the like. It is also preferable that the purity of nitrogen,oxygen, or the rare gas which is introduced into a heat treatmentapparatus be set to greater than or equal to 6N (99.9999%), preferablygreater than or equal to 7N (99.99999%) (that is, the impurityconcentration is lower than or equal to 1 ppm, preferably lower than orequal to 0.1 ppm).

In the case of performing heat treatment after formation of the oxidesemiconductor film, oxygen that is one of main component materialsincluded in the oxide semiconductor might be reduced. However, duringthe heat treatment in this step, oxygen can be supplied to the oxidesemiconductor film 103 from the gate insulating film 102 which is formedusing oxidized material containing silicon; thus, oxygen vacancies inthe oxide semiconductor film 103 can be filled.

By performing the heat treatment as described above, the oxidesemiconductor film 103 can be highly purified so as not to containimpurities other than main components as little as possible. Inaddition, the highly purified oxide semiconductor film 103 includesextremely few (close to zero) carriers derived from a donor, and thecarrier concentration thereof is lower than 1×10¹⁴/cm³, preferably lowerthan 1×10¹²/cm³, further preferably lower than 1×10¹¹/cm³. In such amanner, the oxide semiconductor film 103 that becomes an i-type(intrinsic) oxide semiconductor can be formed.

Through the above steps, the transistor 110 is formed (see FIG. 4E). Inthe transistor 110, the concentration of impurities such as silicontaken into the region 103 a of the oxide semiconductor film 103 issmall. Thus, the transistor 110 can have stable electriccharacteristics.

A planarization insulating film may be formed over the transistor 110.For the planarization insulating film, a heat-resistant organic materialsuch as an acrylic resin, a polyimide resin, a benzocyclobutene-basedresin, a polyamide resin, or an epoxy resin can be used. Other than suchorganic materials, it is also possible to use a low-dielectric constantmaterial (a low-k material), a siloxane-based resin, PSG(phosphosilicate glass), BPSG (borophosphosilicate glass), or the like.Note that the planarization insulating film may be formed by stacking aplurality of insulating films formed of any of these materials.

<Manufacturing Process of Transistor 130>

Next, an example of a manufacturing process of the transistor 130 inFIGS. 3A and 3B will be described with reference to FIGS. 5A to 5E.

First, over the substrate 100, the gate electrode 101, the gateinsulating film 102, and the oxide semiconductor film 103 including theregion 103 a and the region 103 b are formed by steps similar to those(up to the step illustrated in FIG. 4C) of the transistor 110 (see FIG.5A). For the details of the substrate 100, the gate electrode 101, thegate insulating film 102, and the oxide semiconductor film 103, thedescription with reference to FIGS. 4A to 4C can be referred to.

Next, an insulating film 107 used for a channel protective film isformed to a thickness greater than or equal to 5 nm and less than orequal to 300 nm (see FIG. 5B). As the insulating film 107, an inorganicinsulating film containing oxygen is preferably used. For example, aninsulating film such as a silicon oxide film, a silicon oxynitride film,an aluminum oxide film, an aluminum oxynitride film, a gallium oxidefilm, or a hafnium oxide film can be used. There is no particularlimitation on a method for forming the insulating film 107; for example,a sputtering method, a MBE method, a CVD method, a pulse laserdeposition method, an ALD method, or the like can be used asappropriate.

Next, a resist mask is formed over the insulating film 107 by aphotolithography step, the channel protective film 108 is formed byetching, and then, the resist mask is removed (see FIG. 5C). Note that aresist mask used for forming the channel protective film 108 may beformed by an inkjet method. Formation of the resist mask by an inkjetmethod needs no photomask; thus, manufacturing cost can be reduced. Notethat the etching of the channel protective film 108 may be performedusing either dry etching or wet etching, or using both dry etching andwet etching.

As illustrated in FIG. 5C, an end portion of the channel protective film108 preferably has a taper angle greater than or equal to 10° less thanor equal to 60°. The channel protective film 108 is formed to have sucha shape, whereby the field concentration in the vicinity of a lower endportion of the channel protective film 108 can be relaxed.

As described above, the channel protective film 108 is provided over andin contact with the oxide semiconductor film 103, so that damage on theback channel side of the oxide semiconductor film 103, which is causedby etching the source electrode 105 a and the drain electrode 105 b(e.g., damage caused by plasma or an etchant in the etching step), canbe prevented. Accordingly, a semiconductor device including an oxidesemiconductor and having stable electric characteristics can beprovided.

Next, a conductive film used for a source electrode and a drainelectrode (as well as a wiring formed in the same layer as the gateelectrode) is formed over the channel protective film 108 and the oxidesemiconductor film 103. Then, the conductive film is selectively etchedby a photolithography step, so that the source electrode 105 a and thedrain electrode 105 b are formed (see FIG. 5D). This step can beperformed in a manner similar to the step illustrated in FIG. 4D; thus,for the details of the source electrode 105 a and the drain electrode105 b, the description with reference to FIG. 4D can be referred to.

Next, the protective insulating film 109 is formed to cover the sourceelectrode 105 a, the drain electrode 105 b, and the channel protectivefilm 108 (see FIG. 5E). This step can be performed in a manner similarto the step illustrated in FIG. 4E; thus for the details of theprotective insulating film 109, the description with reference to FIG.4E can be referred to.

As described above, the oxide semiconductor film is formed, whereby theconcentration of impurities included in the oxide semiconductor film inthe vicinity of the formed film surface can be reduced. In addition,crystallization of the oxide semiconductor film 103 can be progressed inthe vicinity of the formed film surface; thus, crystallinity of theoxide semiconductor film 103 can be improved. In the case where theoxide semiconductor film 103 is a CAAC-OS film, a crystal portion can beformed even in the vicinity of the formed film surface. Note that in thecrystal portion, a c-axis is aligned in a direction perpendicular to theinterface between the oxide semiconductor film 103 and the gateinsulating film 102 or the interface between the oxide semiconductorfilm 103 and the protective insulating film 109. By using such an oxidesemiconductor film, a highly reliable semiconductor device having stableelectric characteristics can be provided.

The methods and structures described in this embodiment can be combinedas appropriate with any of the methods and structures described in theother embodiments.

Embodiment 2

A semiconductor device (also referred to as a display device) with adisplay function can be manufactured using the transistor an example ofwhich is described in Embodiment 1. Moreover, some or all of the drivercircuits which include the transistor can be formed over a substratewhere the pixel portion is formed, whereby a system-on-panel can beobtained.

In FIG. 9A, a sealant 4005 is provided so as to surround a pixel portion4002 provided over a first substrate 4001, and the pixel portion 4002 issealed by using a second substrate 4006. In FIG. 9A, a signal linedriver circuit 4003 and a scan line driver circuit 4004 which are eachformed using a single crystal semiconductor film or a polycrystallinesemiconductor film over a substrate separately prepared are mounted in aregion that is different from the region surrounded by the sealant 4005over the first substrate 4001. Further, a variety of signals andpotentials are supplied to the signal line driver circuit 4003 and thescan line driver circuit 4004, which are separately formed, or the pixelportion 4002 from flexible printed circuits (FPCs) 4018 a and 4018 b.

In FIGS. 9B and 9C, the sealant 4005 is provided so as to surround thepixel portion 4002 and the scan line driver circuit 4004 which areprovided over the first substrate 4001. The second substrate 4006 isprovided over the pixel portion 4002 and the scan line driver circuit4004. Consequently, the pixel portion 4002 and the scan line drivercircuit 4004 are sealed together with the display element, by the firstsubstrate 4001, the sealant 4005, and the second substrate 4006. InFIGS. 9B and 9C, the signal line driver circuit 4003 which is formedusing a single crystal semiconductor film or a polycrystallinesemiconductor film over a substrate separately prepared is mounted in aregion that is different from the region surrounded by the sealant 4005over the first substrate 4001. In FIGS. 9B and 9C, various signals andpotential are supplied to the signal line driver circuit 4003 which isseparately formed, the scan line driver circuit 4004, and the pixelportion 4002 from an FPC 4018.

Although FIGS. 9B and 9C each illustrate an example in which the signalline driver circuit 4003 is formed separately and mounted on the firstsubstrate 4001, one embodiment of the present invention is not limitedto this structure. The scan line driver circuit may be separately formedand then mounted, or only part of the signal line driver circuit or partof the scan line driver circuit may be separately formed and thenmounted.

Note that a connection method of a separately formed driver circuit isnot particularly limited, and a chip on glass (COG) method, a wirebonding method, a tape automated bonding (TAB) method or the like can beused. FIG. 9A illustrates an example in which the signal line drivercircuit 4003 and the scan line driver circuit 4004 are mounted by a COGmethod. FIG. 9B illustrates an example in which the signal line drivercircuit 4003 is mounted by a COG method. FIG. 9C illustrates an examplein which the signal line driver circuit 4003 is mounted by a TAB method.

In addition, the display device includes a panel in which the displayelement is sealed, and a module in which an IC or the like including acontroller is mounted on the panel.

Note that a display device in this specification means an image displaydevice, a display device, or a light source (including a lightingdevice).

Furthermore, the display device also includes the following modules inits category: a module to which a connector such as an FPC, a TAB tape,or a TCP is attached; a module having a TAB tape or a TCP at the tip ofwhich a printed wiring board is provided; and a module in which anintegrated circuit (IC) is directly mounted on a display element by aCOG method.

The pixel portion and the scan line driver circuit provided over thefirst substrate include a plurality of transistors, and the transistordescribed in Embodiment 1 can be applied thereto.

As the display element provided in the display device, a liquid crystalelement (also referred to as a liquid crystal display element) or alight-emitting element (also referred to as a light-emitting displayelement) can be used. The light-emitting element includes, in itscategory, an element whose luminance is controlled by a current or avoltage, and specifically includes, in its category, an inorganicelectroluminescent (EL) element, an organic EL element, and the like.Furthermore, a display medium whose contrast is changed by an electriceffect, such as electronic ink, can be used.

Embodiments of the semiconductor device will be described with referenceto FIG. 10, FIG. 11, and FIG. 12. FIG. 10, FIG. 11, and FIG. 12correspond to cross-sectional views taken along line M-N in FIG. 9B.

As illustrated in FIG. 10, FIG. 11, and FIG. 12, the semiconductordevice includes a connection terminal electrode 4015 and a terminalelectrode 4016. The connection terminal electrode 4015 and the terminalelectrode 4016 are electrically connected to a terminal included in theFPC 4018 through an anisotropic conductive film 4019.

The connection terminal electrode 4015 is formed of the same conductivefilm as a first electrode layer 4030. The terminal electrode 4016 isformed of the same conductive film as a source electrode and a drainelectrode of transistors 4010 and 4011.

Further, the pixel portion 4002 and the scan line driver circuit 4004provided over the first substrate 4001 each include a plurality oftransistors. FIG. 10, FIG. 11, and FIG. 12 each illustrate thetransistor 4010 included in the pixel portion 4002 and the transistor4011 included in the scan line driver circuit 4004.

In this embodiment, any of the transistors described in Embodiment 1 canbe employed for the transistors 4010 and 4011. Variation in the electriccharacteristics of the transistors 4010 and 4011 is suppressed and thetransistors 4010 and 4011 are electrically stable. Thus, as thesemiconductor devices of this embodiment illustrated in FIG. 10, FIG.11, and FIG. 12, a highly reliable semiconductor device can be provided.

The transistor 4011 included in the scan line driver circuit 4004 has astructure in which a second gate electrode is formed over an insulatingfilm 4034. A voltage applied to the second gate electrode is controlled,whereby the threshold voltage of the transistor 4011 can be controlled.

The transistor 4010 included in the pixel portion 4002 is electricallyconnected to a display element to form a display panel. A variety ofdisplay elements can be used as the display element as long as displaycan be performed.

An example of a liquid crystal display device using a liquid crystalelement as a display element is illustrated in FIG. 10. In FIG. 10, aliquid crystal element 4013 which is a display element includes a firstelectrode layer 4030, a second electrode layer 4031, and a liquidcrystal layer 4008. Note that the insulating films 4032 and 4033functioning as alignment films are provided so that the liquid crystallayer 4008 is interposed therebetween. The second electrode layer 4031is provided on the second substrate 4006 side, and the first electrodelayer 4030 and the second electrode layer 4031 are stacked, with theliquid crystal layer 4008 interposed therebetween.

A spacer 4035 is a columnar spacer which is obtained by selectiveetching of an insulating film and is provided in order to control thethickness (a cell gap) of the liquid crystal layer 4008. Alternatively,a spherical spacer may be used.

In the case where a liquid crystal element is used as the displayelement, a thermotropic liquid crystal, a low-molecular liquid crystal,a high-molecular liquid crystal, a polymer dispersed liquid crystal, aferroelectric liquid crystal, an anti-ferroelectric liquid crystal, orthe like can be used. Such a liquid crystal material exhibits acholesteric phase, a smectic phase, a cubic phase, a chiral nematicphase, an isotropic phase, or the like depending on a condition.

Alternatively, liquid crystal exhibiting a blue phase for which analignment film is unnecessary may be used. A blue phase is one of liquidcrystal phases, which is generated just before a cholesteric phasechanges into an isotropic phase while temperature of cholesteric liquidcrystal is increased. Since the blue phase appears only in a narrowtemperature range, a liquid crystal composition in which several weightpercent or more of a chiral material is mixed is used for the liquidcrystal layer in order to improve the temperature range. The liquidcrystal composition which includes a liquid crystal exhibiting a bluephase and a chiral material has a short response time of 1 msec or lessand has optical isotropy, which contributes to the exclusion of thealignment process and reduction of viewing angle dependence. Inaddition, since an alignment film does not need to be provided andrubbing treatment is also unnecessary, electrostatic discharge damagecaused by the rubbing treatment can be prevented and defects and damageof the liquid crystal display device in the manufacturing process can bereduced. Thus, productivity of the liquid crystal display device can beincreased.

The specific resistivity of the liquid crystal material is 1×10⁹ Ω·cm ormore, preferably 1×10¹¹ Ω·cm or more, much preferably 1×10¹² Ω·cm ormore. The value of the specific resistivity in this specification ismeasured at 20° C.

The size of storage capacitor formed in the liquid crystal displaydevice is set considering the leakage current of the transistor providedin the pixel portion or the like so that charge can be held for apredetermined period. By using the transistor including the high-purityoxide semiconductor film, it is enough to provide a storage capacitorhaving a capacitance that is ⅓ or less, preferably ⅕ or less of a liquidcrystal capacitance of each pixel.

In the transistor used in this embodiment, which includes the highlypurified oxide semiconductor film, the current in an off state (theoff-state current) can be made small. Accordingly, an electrical signalsuch as an image signal can be held for a longer period in the pixel,and a writing interval can be set longer in an on state. Therefore,frequency of refresh operation can be reduced, which leads to an effectof suppressing power consumption.

In addition, the transistor including the highly purified oxidesemiconductor film used in this embodiment can have relatively highfield-effect mobility and thus can operate at high speed. Therefore, byusing the transistor in a pixel portion of a liquid crystal displaydevice, a high-quality image can be provided. In addition, since thetransistors can be separately provided in a driver circuit portion and apixel portion over one substrate, the number of components of the liquidcrystal display device can be reduced.

For the liquid crystal display device, a twisted nematic (TN) mode, anin-plane-switching (IPS) mode, a fringe field switching (FFS) mode, anaxially symmetric aligned micro-cell (ASM) mode, an optical compensatedbirefringence (OCB) mode, a ferroelectric liquid crystal (FLC) mode, anantiferroelectric liquid crystal (AFLC) mode, or the like can be used.

A normally black liquid crystal display device such as a transmissiveliquid crystal display device utilizing a vertical alignment (VA) modeis preferable. The vertical alignment mode is a method of controllingalignment of liquid crystal molecules of a liquid crystal display panel,in which liquid crystal molecules are aligned vertically to a panelsurface when no voltage is applied. Some examples are given as thevertical alignment mode; for example, a multi-domain vertical alignment(MVA) mode, a patterned vertical alignment (PVA) mode, an advancedsuper-view (ASV) mode, or the like can be employed. Moreover, it ispossible to use a method called domain multiplication or multi-domaindesign, in which a pixel is divided into some regions (subpixels) andmolecules are aligned in different directions in their respectiveregions.

In the display device, a black matrix (a light-blocking layer), anoptical member (an optical substrate) such as a polarizing member, aretardation member, or an anti-reflection member, and the like areprovided as appropriate. For example, circular polarization may beobtained by using a polarizing substrate and a retardation substrate. Inaddition, a backlight, a side light, or the like may be used as a lightsource.

In addition, it is possible to employ a time-division display method(also called a field-sequential driving method) with use of a pluralityof light-emitting diodes (LEDs) as a backlight. By employing afield-sequential driving method, color display can be performed withoutusing a color filter.

As a display method in the pixel portion, a progressive method, aninterlace method or the like can be employed. Further, color elementscontrolled in a pixel at the time of color display are not limited tothree colors: R, G, and B (R, G, and B correspond to red, green, andblue, respectively). For example, R, G, B, and W (W corresponds towhite); R, G, B, and one or more of yellow, cyan, magenta, and the like;or the like can be used. Further, the sizes of display regions may bedifferent between respective dots of color elements. However, oneembodiment of the present invention is not limited to a color displaydevice and can be applied to a monochrome display device.

Alternatively, as the display element included in the display device, alight-emitting element utilizing electroluminescence can be used.Light-emitting elements utilizing electroluminescence are classified inaccordance with whether a light-emitting material is an organic compoundor an inorganic compound. In general, the former is referred to as anorganic EL element, and the latter is referred to as an inorganic ELelement.

In an organic EL element, by application of voltage to a light-emittingelement, electrons and holes are separately injected from a pair ofelectrodes into a layer containing a light-emitting organic compound,and current flows. The carriers (electrons and holes) are recombined,and thus, the light-emitting organic compound is excited. Thelight-emitting organic compound returns to a ground state from theexcited state, thereby emitting light. Owing to such a mechanism, thislight-emitting element is referred to as a current-excitationlight-emitting element.

The inorganic EL elements are classified in accordance with theirelement structures into a dispersion-type inorganic EL element and athin-film inorganic EL element. A transistor and a light-emittingelement are formed over a substrate. A dispersion-type inorganic ELelement has a light-emitting layer where particles of a light-emittingmaterial are dispersed in a binder, and its light emission mechanism isdonor-acceptor recombination type light emission that utilizes a donorlevel and an acceptor level. A thin-film inorganic EL element has astructure where a light-emitting layer is sandwiched between dielectriclayers, which are further sandwiched between electrodes, and its lightemission mechanism is localized type light emission that utilizesinner-shell electron transition of metal ions. Note that an example ofan organic EL element as a light-emitting element is described here.

In order to extract light emitted from the light-emitting element, it isacceptable as long as at least one of a pair of electrodes istransparent. The light-emitting element can have a top emissionstructure in which light emission is extracted through the surfaceopposite to the substrate; a bottom emission structure in which lightemission is extracted through the surface on the substrate side; or adual emission structure in which light emission is extracted through thesurface opposite to the substrate and the surface on the substrate side,and a light-emitting element having any of these emission structures canbe used.

An example of a light-emitting device using a light-emitting element asa display element is illustrated in FIG. 11. A light-emitting element4513 that is a display element is electrically connected to thetransistor 4010 provided in the pixel portion 4002. A structure of thelight-emitting element 4513 is not limited to the illustratedstacked-layer structure including the first electrode layer 4030, anelectroluminescent layer 4511, and the second electrode layer 4031. Thestructure of the light-emitting element 4513 can be changed asappropriate depending on a direction in which light is extracted fromthe light-emitting element 4513, or the like.

A partition wall 4510 can be formed using an organic insulating materialor an inorganic insulating material. It is particularly preferable thatthe partition wall 4510 be formed using a photosensitive resin materialto have an opening over the first electrode layer 4030 so that asidewall of the opening is formed as a tilted surface with continuouscurvature.

The electroluminescent layer 4511 may be formed using a single layer ora plurality of layers stacked.

A protective film may be formed over the second electrode layer 4031 andthe partition wall 4510 in order to prevent entry of oxygen, hydrogen,moisture, carbon dioxide, or the like into the light-emitting element4513. As the protective film, a silicon nitride film, a silicon nitrideoxide film, a DLC film, or the like can be formed. In addition, in aspace which is formed with the first substrate 4001, the secondsubstrate 4006, and the sealant 4005, a filler 4514 is provided forsealing. It is preferable that a panel be packaged (sealed) with aprotective film (such as a laminate film or an ultraviolet curable resinfilm) or a cover material with high air-tightness and littledegasification so that the panel is not exposed to the outside air, inthis manner.

As the filler 4514, an ultraviolet curable resin or a thermosettingresin can be used as well as an inert gas such as nitrogen or argon.Examples of such a resin include polyvinyl chloride (PVC), an acrylicresin, a polyimide resin, an epoxy resin, a silicone resin, polyvinylbutyral (PVB), and ethylene vinyl acetate (EVA). For example, nitrogenis used for the filler.

In addition, if needed, an optical film such as a polarizing plate, acircularly polarizing plate (including an elliptically polarizingplate), a retardation plate (a quarter-wave plate or a half-wave plate),or a color filter may be provided as appropriate on a light-emittingsurface of the light-emitting element. Further, the polarizing plate orthe circularly polarizing plate may be provided with an anti-reflectionfilm. For example, anti-glare treatment by which reflected light can bediffused by projections and depressions on the surface so as to reducethe glare can be performed.

Further, an electronic paper in which electronic ink is driven can beprovided as the display device. The electronic paper is also referred toas an electrophoretic display device (an electrophoretic display) and isadvantageous in that it has the same level of readability as plainpaper, it has lower power consumption than other display devices, and itcan be made thin and lightweight.

An electrophoretic display device can have various modes. Anelectrophoretic display device contains a plurality of microcapsulesdispersed in a solvent or a solute, and each microcapsule contains firstparticles which are positively charged and second particles which arenegatively charged. By applying an electric field to the microcapsules,the particles in the microcapsules move in opposite directions to eachother and only the color of the particles gathering on one side isdisplayed. Note that the first particles and the second particles eachcontain pigment and do not move without an electric field. Moreover, thefirst particles and the second particles have different colors (whichmay be colorless).

Thus, an electrophoretic display device is a display device thatutilizes a so-called dielectrophoretic effect by which a substancehaving a high dielectric constant moves to a high-electric field region.

A solution in which the above microcapsules are dispersed in a solventis referred to as electronic ink. This electronic ink can be printed ona surface of glass, plastic, cloth, paper, or the like. Furthermore, byusing a color filter or particles that have a pigment, color display canalso be achieved.

Note that the first particles and the second particles in themicrocapsules may each be formed of a single material selected from aconductive material, an insulating material, a semiconductor material, amagnetic material, a liquid crystal material, a ferroelectric material,an electroluminescent material, an electrochromic material, and amagnetophoretic material, or formed of a composite material of any ofthese.

As the electronic paper, a display device using a twisting ball displaysystem can be used. The twisting ball display system refers to a methodin which spherical particles each colored in black and white arearranged between a first electrode layer and a second electrode layerwhich are electrode layers used for a display element, and a potentialdifference is generated between the first electrode layer and the secondelectrode layer to control orientation of the spherical particles, sothat display is performed.

FIG. 12 illustrates an active matrix electronic paper as one embodimentof a semiconductor device. The electronic paper in FIG. 12 is an exampleof a display device using a twisting ball display system.

Between the first electrode layer 4030 connected to the transistor 4010and the second electrode layer 4031 provided on the second substrate4006, spherical particles 4613 each of which includes a black region4615 a, a white region 4615 b, and a cavity 4612 which is filled withliquid around the black region 4615 a and the white region 4615 b, areprovided. A space around the spherical particles 4613 is filled with afiller 4614 such as a resin. The second electrode layer 4031 correspondsto a common electrode (counter electrode). The second electrode layer4031 is electrically connected to a common potential line.

Note that in FIG. 10, FIG. 11, and FIG. 12, a flexible substrate as wellas a glass substrate can be used as the first substrate 4001 and thesecond substrate 4006. For example, a light-transmitting plasticsubstrate or the like can be used. As plastic, a fiberglass-reinforcedplastics (FRP) plate, a polyvinyl fluoride (PVF) film, a polyester film,or an acrylic resin film can be used. In addition, a sheet with astructure in which an aluminum foil is sandwiched between PVF films orpolyester films can be used.

An insulating layer 4021 can be formed using an inorganic insulatingmaterial or an organic insulating material. Note that the insulatinglayer 4021 formed using a heat-resistant organic insulating materialsuch as an acrylic resin, a polyimide resin, a benzocyclobutene resin, apolyamide resin, or an epoxy resin is preferably used as a planarizinginsulating film. Other than such organic insulating materials, it ispossible to use a low-dielectric constant material (a low-k material), asiloxane-based resin, phosphosilicate glass (PSG), borophosphosilicateglass (BPSG), or the like. The insulating layer may be formed bystacking a plurality of insulating films formed of these materials.

There is no particular limitation on the method for forming theinsulating layer 4021, and the insulating layer can be formed, dependingon the material, by a sputtering method, a spin coating method, adipping method, spray coating, a droplet discharge method (e.g., aninkjet method or the like), a printing method (e.g., screen printing,offset printing, or the like), roll coating, curtain coating, knifecoating, or the like.

The display device displays an image by transmitting light from a lightsource or a display element. Thus, the substrates and the thin filmssuch as insulating films and conductive films provided in the pixelportion where light is transmitted have light-transmitting propertieswith respect to light in the visible-light wavelength range.

The first electrode layer 4030 and the second electrode layer 4031 (eachof which may be called a pixel electrode layer, a common electrodelayer, a counter electrode layer, or the like) for applying voltage tothe display element may have light-transmitting properties orlight-reflecting properties, which depends on the direction in whichlight is extracted, the position where the electrode layer is provided,the pattern structure of the electrode layer, and the like.

The first electrode layer 4030 and the second electrode layer 4031 canbe formed using a light-transmitting conductive material such as indiumoxide containing tungsten oxide, indium zinc oxide containing tungstenoxide, indium oxide containing titanium oxide, indium tin oxidecontaining titanium oxide, indium tin oxide (hereinafter referred to asITO), indium zinc oxide, or indium tin oxide to which silicon oxide isadded.

The first electrode layer 4030 and the second electrode layer 4031 canbe formed of one or more kinds of materials selected from metals such astungsten (W), molybdenum (Mo), zirconium (Zr), hafnium (Hf), vanadium(V), niobium (Nb), tantalum (Ta), chromium (Cr), cobalt (Co), nickel(Ni), titanium (Ti), platinum (Pt), aluminum (Al), copper (Cu), andsilver (Ag); alloys of these metals; and nitrides of these metals.

A conductive composition containing a conductive high molecule (alsoreferred to as conductive polymer) can be used for the first electrodelayer 4030 and the second electrode layer 4031. As the conductive highmolecule, a so-called 7 c-electron conjugated conductive polymer can beused. For example, polyaniline or a derivative thereof, polypyrrole or aderivative thereof, polythiophene or a derivative thereof, and acopolymer of two or more of aniline, pyrrole, and thiophene or aderivative thereof can be given.

Since the transistor is easily broken owing to static electricity or thelike, a protective circuit for protecting the driver circuit ispreferably provided. The protective circuit is preferably formed using anonlinear element.

As described above, by using any of the transistors described inEmbodiment 1, a semiconductor device having a high reliability can beprovided. Note that the transistors described in Embodiment 1 can beapplied to not only semiconductor devices having the display functionsdescribed above but also semiconductor devices having a variety offunctions, such as a power device which is mounted on a power supplycircuit, a semiconductor integrated circuit such as an LSI, and asemiconductor device having an image sensor function of readinginformation of an object.

The methods and structures described in this embodiment can be combinedas appropriate with any of the methods and structures described in theother embodiments.

Embodiment 3

A semiconductor device disclosed in this specification and the like canbe applied to a variety of electronic devices (including game machines).Examples of electronic devices are a television set (also referred to asa television or a television receiver), a monitor of a computer or thelike, a camera such as a digital camera or a digital video camera, adigital photo frame, a mobile phone handset (also referred to as amobile phone or a mobile phone device), a portable game machine, aportable information terminal, an audio reproducing device, alarge-sized game machine such as a pachinko machine, and the like.Examples of electronic devices each including the liquid crystal displaydevice described in the above embodiment are described.

FIG. 13A illustrates a laptop personal computer, which includes a mainbody 3001, a housing 3002, a display portion 3003, a keyboard 3004, andthe like. By applying the semiconductor device described in Embodiment 1or 2, the laptop personal computer can have high reliability.

FIG. 13B illustrates a personal digital assistant (PDA) including adisplay portion 3023, an external interface 3025, an operation button3024, and the like in a main body 3021. A stylus 3022 is included as anaccessory for operation. By applying the semiconductor device describedin Embodiment 1 or 2, the portable digital assistant (PDA) can havehigher reliability.

FIG. 13C illustrates an example of an e-book reader. For example, ane-book reader 2700 includes two housings, a housing 2701 and a housing2703. The housing 2701 and the housing 2703 are combined with a hinge2711 so that the e-book reader 2700 can be opened and closed with thehinge 2711 as an axis. With such a structure, the e-book reader 2700 canoperate like a paper book.

A display portion 2705 and a display portion 2707 are incorporated inthe housing 2701 and the housing 2703, respectively. The display portion2705 and the display portion 2707 may display one image or differentimages. In the case where the display portion 2705 and the displayportion 2707 display different images, for example, a display portion onthe right side (the display portion 2705 in FIG. 13C) can display textand a display portion on the left side (the display portion 2707 in FIG.13C) can display images. By applying the semiconductor device describedin Embodiment 1 or 2, the electronic book reader 2700 can have highreliability.

In FIG. 13C, the housing 2701 includes an operation portion and the likeas an example. For example, the housing 2701 is provided with a powerswitch 2721, operation keys 2723, a speaker 2725, and the like. With theoperation key 2723, pages can be turned. Note that a keyboard, apointing device, or the like may also be provided on the surface of thehousing, on which the display portion is provided. Furthermore, anexternal connection terminal (an earphone terminal, a USB terminal, orthe like), a recording medium insertion portion, and the like may beprovided on the back surface or the side surface of the housing.Moreover, the e-book reader 2700 may have a function of an electronicdictionary.

The e-book reader 2700 may have a configuration capable of wirelesslytransmitting and receiving data. Through wireless communication, desiredbook data or the like can be purchased and downloaded from an electronicbook server.

FIG. 13D illustrates a smartphone, which includes a housing 2800, abutton 2801, a microphone 2802, a display portion 2803 provided with atouch panel, a speaker 2804, and a camera lens 2805 and functions as amobile phone. By applying the semiconductor device described inEmbodiment 1 or 2, the smartphone can have high reliability.

The display direction of the display portion 2803 can be changeddepending on a usage pattern. Since the camera lens 2805 is provided onthe same plane as the display portion 2803, videophone is possible. Thespeaker 2804 and the microphone 2802 can be used for operations such asvideo calls, sound recording, and playback without being limited to thevoice call function.

An external connection terminal 2806 can be connected to an AC adapterand various types of cables such as a USB cable, and charging and datacommunication with a personal computer are possible. Furthermore, alarge amount of data can be stored and moved by inserting a storagemedium into the external memory slot (not illustrated).

Further, in addition to the above functions, an infrared communicationfunction, a television reception function, or the like may be provided.

FIG. 13E illustrates a digital video camera which includes a main body3051, a display portion A 3057, an eyepiece 3053, an operation switch3054, a display portion B 3055, a battery 3056, and the like. Byapplying the semiconductor device described in Embodiment 1 or 2, thedigital video camera can have high reliability.

FIG. 13F illustrates an example of a television set. In a television set9600, a display portion 9603 is incorporated in a housing 9601. Thedisplay portion 9603 can display images. Here, the housing 9601 issupported by a stand 9605. By applying the semiconductor devicedescribed in Embodiment 1 or 2, the television set 9600 can have highreliability.

The television set 9600 can be operated by an operation switch of thehousing 9601 or a separate remote controller. Further, the remotecontroller may be provided with a display portion for displaying dataoutput from the remote controller.

Note that the television set 9600 is provided with a receiver, a modem,and the like. With use of the receiver, general television broadcastingcan be received. Moreover, when the display device is connected to acommunication network with or without wires via the modem, one-way (froma sender to a receiver) or two-way (between a sender and a receiver orbetween receivers) information communication can be performed.

The methods and structures described in this embodiment can be combinedas appropriate with any of the methods and structures described in theother embodiments.

Example 1

In this example, results of SIMS measurement of the concentration ofsilicon included in an oxide target will be described.

First, oxide targets used in this example are described.

As Sample A, an In—Ga—Zn-based oxide target (atomic ratio:In:Ga:Zn=2:1:3) was used. As Sample B, an In—Ga—Zn-based oxide target(atomic ratio: In:Ga:Zn=3:1:2) was used. As Sample C, an In—Sn—Zn-basedoxide (atomic ratio: In:Sn:Zn=2:1:3) was used. In addition, as StandardSample D, an In—Ga—Zn-based oxide target (atomic ratio: In:Ga:Zn=1:1:1)to which silicon is added was used.

SIMS measurement was performed on Sample A, Sample B, Sample C, andStandard Sample D, so that the concentration of silicon included in eachsample was measured.

FIG. 14 shows results of SIMS measurement of Samples A to C and StandardSample D.

As seen in FIG. 14, the concentration of silicon in Sample A is 4×10¹⁸atoms/cm³, the concentration of silicon in Sample B is 3×10¹⁷ atoms/cm³,the concentration of silicon in Sample C is 2×10¹⁷ atoms/cm³, and theconcentration of silicon in Standard Sample D is 2×10¹⁸ atoms/cm³. Notethat the results of SIMS measurement of Samples A to C were quantifiedusing Standard Sample D.

In the case where an oxide semiconductor film is deposited using any ofSamples A to C and Standard Sample D, the above data can be used as amaterial for estimating whether silicon other than silicon in a target(e.g., silicon entered the oxide semiconductor film from an insulatingfilm by mixing) is included in the oxide semiconductor film or not.

For example, in the case where in an oxide semiconductor film depositedusing Sample A (an oxide target where In:Ga:Zn=2:1:3 (atomic ratio)) asa target, the concentration of silicon in the film is higher than 4×10¹⁸atoms/cm³, it is found that silicon enters the oxide semiconductor filmfrom a portion other than the target.

Example 2

The above embodiment describes that entry of an element that is aconstituent element of an insulating film into an oxide semiconductorfilm is caused by mixing occurring in deposition of the oxidesemiconductor film. However, as another cause, it can be considered thatan element that is a constituent element of an insulating film diffusesinto the oxide semiconductor film by heating a substrate afterdeposition of the oxide semiconductor film. Thus, in this example,experiment for examining whether entry of an element that is aconstituent element of an insulating film into an oxide semiconductorfilm is caused by thermal diffusion will be described.

For the experiment, first, three substrates (over each of thesubstrates, an insulating film and an oxide semiconductor film wereformed) were prepared. Then, a sample which was not subjected to heattreatment (hereinafter, called Sample E), a sample which was subjectedto heat treatment at 450° C. (hereinafter, called Sample F), and asample which was subjected to heat treatment at 650° C. (hereinafter,called Sample G) were manufactured. After that, in each sample, theconcentration of silicon in the oxide semiconductor film in the vicinityof an interface with the gate insulating film was measured using atime-of-flight secondary ion mass spectrometer (ToF-SIMS).

A structure of a sample used for ToF-SIMS measurement is illustrated inFIG. 15.

The sample illustrated in FIG. 15 was obtained by depositing a siliconoxide film 202 over a silicon substrate 200, improving planarity of asurface with use of a chemical mechanical polishing (CMP) apparatus,depositing an IGZO film 204, and performing heat treatment.

The silicon oxide film 202 was deposited with a sputtering apparatus.The conditions for depositing the silicon oxide film 202 were asfollows: substrate temperature, 100° C.; gas flow rate, Ar/O₂=25 sccm/25sccm; deposition power, 1.5 kW (RF power supply); deposition pressure,0.4 Pa; and thickness, 300 nm. As a sputtering target, a silicon oxidetarget was used. Note that before the silicon oxide film 202 was formed,an oxide film formed over the surface of the silicon substrate 200 wasremoved using diluted hydrofluoric acid.

The IGZO film 204 was deposited with a sputtering apparatus. Theconditions for depositing the IGZO film 204 were as follows: substratetemperature, 200° C.; gas flow rate, Ar/O₂=30 sccm/15 sccm; depositionpower, 0.5 kW (DC power supply); deposition pressure, 0.4 Pa; andthickness, 15 nm. Note that as a sputtering target, an oxide target(In:Ga:Zn=3:1:2 (atomic ratio)) was used.

The substrate was introduced into an electric furnace using a resistanceheater or the like, and then the heat treatment was performed. Thetreatment conditions of Sample F were as follows: heating temperature,450° C.; and heating time, one hour. The treatment conditions of SampleG were as follows: heating temperature, 650° C.; and heating time, onehour. Note that the heating atmosphere of both samples was a mixedatmosphere of nitrogen and oxygen. Sample E was not subjected to heattreatment.

Next, Samples E to G were subjected to ToF-SIMS measurement from thesubstrate surface side (on the IGZO film 204 side), so that theconcentration of silicon in the IGZO film in the vicinity of theinterface with the silicon oxide film was measured. FIG. 16 showsresults thereof.

The results shown in FIG. 16 indicates that in all the samples, theconcentration of silicon in the oxide semiconductor film in the vicinityof the interface with the silicon oxide film is higher than 3×10¹⁷atoms/cm³, the value of which is the concentration of silicon includedin the In—Ga—Zn-based oxide target (In:Ga:Zn=3:1:2 (atomic ratio))described in Example 1. Thus, it is found that silicon measured in theoxide semiconductor film in the vicinity of the interface with thesilicon oxide film is not derived from the In—Ga—Zn-based oxide target.

In addition, as seen in FIG. 16, a significant difference of theinclination of the concentration of silicon (also referred to as siliconconcentration gradient) in the IGZO film in the vicinity of theinterface is not observed, between the sample which was not subjected toheat treatment (Sample E) and the samples which were subjected to heattreatment (Sample F and Sample G). Thus, entry of an element that is aconstituent element of the insulating film into the oxide semiconductorfilm is caused not by thermal diffusion but by mixing.

Example 3

An experiment was conducted to examine whether entry of a constituentelement of an insulating film into an oxide semiconductor film, which iscaused by mixing, can be suppressed by decreasing the power fordepositing the oxide semiconductor film. In this example, the experimentwill be described.

In the experiment, four samples were manufactured in the followingmanner: first, insulating films were formed over substrates; four oxidesemiconductor films were deposited over the respective insulating filmswith different power conditions (1 kW, 5 kW, 9 kW, and (1 kW+5 kW)); andheat treatment was performed on each substrate. Then, the concentrationof silicon in the oxide semiconductor film in the vicinity of aninterface with a gate insulating film of each sample was measured with aToF-SIMS method.

FIG. 17 illustrates a structure of the sample used for ToF-SIMSmeasurement.

The sample illustrated in FIG. 17 was obtained by depositing a siliconoxynitride film 302 over a substrate 300, depositing an IGZO film 304,and performing heat treatment.

The silicon oxynitride film 302 was deposited with use of a high-densityplasma CVD apparatus. The conditions for depositing the siliconoxynitride film 302 were as follows: substrate temperature, 325° C.; gasflow rate, SiH₄/N₂O/Ar=250 sccm/2500 sccm/2500 sccm; deposition power, 5kW (four microwave power sources were used for the respective samples);deposition pressure, 30 Pa; and thickness, 100 nm. Note that the surfaceof the glass substrate 300 was cleaned to remove particles and the likebefore formation of the silicon oxynitride film 302.

The IGZO film 304 was deposited with use of a sputtering apparatus. Theconditions for depositing the IGZO film 304 were as follows: substratetemperature, 170° C.; gas flow rate, Ar/02=100 sccm/100 sccm; depositionpressure, 0.6 Pa; thickness, 35 nm; and deposition power, fourconditions of 1 kW, 5 kW, 9 kW, and (1 kW+5 kW) (an AC power source wasused for each sample). Note that as a sputtering target, an oxide target(In:Ga:Zn=1:1:1 [atomic ratio]) was used.

Note that the above deposition power “1 kW+5 kW” means that a power of 1kW was used for a 5-nm-thick film deposition and then a power of 5 kWwas used for a 30-nm-thick film deposition. Hereinafter, a sample inwhich an oxide semiconductor film was deposited with 9 kW is referred toas Sample H, a sample in which an oxide semiconductor film was depositedwith 5 kW is referred to as Sample I, a sample in which an oxidesemiconductor film was deposited with 1 kW is referred to as Sample J,and a sample in which an oxide semiconductor film was deposited with (1kW+5 kW) is referred to as Sample K.

The substrates were introduced into an electric furnace using aresistance heater or the like, and heat treatment was performed. Theheat treatment was performed first for one hour at a temperature of 450°C. in an N₂ atmosphere, and then performed for one hour at a temperatureof 650° C. in a (N₂+O₂) atmosphere.

Next, Sample H to Sample K were subjected to ToF-SIMS measurement fromthe substrate surface side (the IGZO film 304 side) to measure thesilicon concentration in the IGZO film in the vicinity of an interfacewith the silicon oxynitride film. The results are shown in FIGS. 18A and18B. Note that FIG. 18B shows part of FIG. 18A which is enlarged.

From FIGS. 18A and 18B, it can be found that in all of the samples, thesilicon concentration in the IGZO film in the vicinity of the interfacewith the silicon oxynitride film is higher than 2×10¹⁸ atoms/cm³, thevalue of which is the silicon concentration in the In—Ga—Zn-based oxidetarget (In:Ga:Zn=1:1:1 [atomic ratio]) described in Example 1. Thus,silicon measured in the IGZO film in the vicinity of the interface withthe silicon oxynitride film is not derived from an In—Ga—Zn-based oxidetarget.

In addition, as can be seen from FIGS. 18A and 18B, the concentration ofsilicon in the IGZO film in the vicinity with the interface with thesilicon oxynitride film tends to decrease as the deposition power isdecreased. According to the above, entry of a constituent element of theinsulating film into the oxide semiconductor film, which is caused bymixing, can be suppressed by decreasing the power for depositing theoxide semiconductor film.

Furthermore, the silicon concentrations of Sample J and Sample K aresubstantially the same, which indicates that entry of a constituentelement of the insulating film into the oxide semiconductor film, whichis caused by mixing, can be suppressed even when deposition of the oxidesemiconductor film is performed with a low power in the initial stageand then the rest of deposition is performed with the increased power.

Example 4

In this example, the measurement results of crystal states in oxidesemiconductor films will be described. The crystal states are generatedby entering an element that is a constituent element of an insulatingfilm into the oxide semiconductor films.

First, two substrates over which oxide semiconductor films were formedwith use of targets having different compositions were prepared, andthen each substrate was divided into three. After that, the substrateseach of which has been divided into three were subjected to heattreatment under different conditions from each other. As a result, sixsamples were manufactured, in total, under different conditions. Then, acrystal state of the oxide semiconductor film in each sample wasmeasured with X-ray diffraction (XRD).

First, a structure of the samples used for XRD measurement isillustrated in FIG. 19A.

The sample illustrated in FIG. 19A was obtained by depositing an IGZOfilm 402 with use of an IGZO (In:Ga:Zn=1:1:1 (atomic ratio)) target towhich SiO₂ was added over a substrate 400 and performing heat treatment.

The IGZO film 402 was deposited with a sputtering apparatus. Theconditions for depositing the IGZO film 402 were as follows: substratetemperature, 200° C.; deposition power, 100 W; deposition pressure, 0.4Pa; gas flow rate, 02=10 sccm; and thickness, 100 nm. Note that assputtering targets, a target (In:Ga:Zn=1:1:1 (atomic ratio)) to whichSiO₂ was added at 2 wt. % and a target (In:Ga:Zn=1:1:1 (atomic ratio))to which SiO₂ was added at 5 wt. % were used. Note that before the IGZOfilm 402 was deposited, the surface of the glass substrate 400 wascleaned, so that particles and the like were removed.

Each substrate was introduced into an electric furnace using aresistance heater or the like, and then the heat treatment wasperformed. One of the three substrates which had been obtained bydivision after deposition of the IGZO film was subjected to heattreatment at 650° C. for one hour in an N₂ atmosphere, and thensubjected to heat treatment at 650° C. for one hour in an O₂ atmosphere.Another of the three substrates obtained by division was subjected toheat treatment at 450° C. for one hour in an N₂ atmosphere, and thensubjected to heat treatment at 450° C. for one hour in an O₂ atmosphere.Further, the other of the three substrates obtained by division was notsubjected to heat treatment.

With use of the above targets, heat treatment was performed under theabove conditions, so that six kinds of samples (Samples L to Q shown inTable 1) were made.

TABLE 1 Sample Target Heat Condition L In:Ga:Zn = 1:1:1 + SiO₂ (2 wt %)<<650° C., N₂ atmosphere, one hour>> + <<650° C., O₂ atmosphere, onehour>> M In:Ga:Zn = 1:1:1 + SiO₂ (2 wt %) <<450° C., N₂ atmosphere, onehour>> + <<450° C., O₂ atmosphere, one hour>> N In:Ga:Zn = 1:1:1 + SiO₂(2 wt %) No Heat Treatment O In:Ga:Zn = 1:1:1 + SiO₂ (5 wt %) <<650° C.,N₂ atmosphere, one hour>> + <<650° C., O₂ atmosphere, one hour>> PIn:Ga:Zn = 1:1:1 + SiO₂ (5 wt %) <<450° C., N₂ atmosphere, one hour>> +<<450° C., O₂ atmosphere, one hour>> Q In:Ga:Zn = 1:1:1 + SiO₂ (5 wt %)No Heat Treatment

Next, XRD measurement was performed on the IGZO films in Samples L to Q,so that a crystal state of each film was measured. Results thereof areshown in FIGS. 20A and 20B. FIG. 20A shows XRD measurement results ofSamples L to N, and FIG. 20B shows XRD measurement results of Samples Oto Q.

As seen in FIG. 20A, Sample L which was subjected to heat treatment at650° C. within the temperature range described in the above has a peakattributed to crystal at around 31° (=2θ). On the other hand, all thesamples shown in FIG. 20B has no peak attributed to crystal. Accordingto the above results, in the IGZO film, crystallization by heattreatment is inhibited when excess silicon is included as impurities.

Next, in order to measure the rate of silicon in an IGZO film depositedwith use of a target to which silicon is added at 2 wt. %, compositionof elements included in the IGZO film were measured with X-rayphotoelectron spectroscopy (XPS).

Each sample used for XPS measurement has a structure in which an IGZOfilm 502 is deposited over a silicon substrate 500 as illustrated inFIG. 19B.

The IGZO film 502 was deposited with a sputtering apparatus. Theconditions for depositing the IGZO film 502 were as follows: substratetemperature, 200° C.; deposition power, 100 W; deposition pressure, 0.4Pa; gas flow rate, O₂=10 sccm; and thickness, 15 nm. Note that as asputtering target, a target (In:Ga:Zn=1:1:1 (atomic ratio)) to whichSiO₂ was added at 2 wt. % was used. Note that before the IGZO film 502was deposited, an oxide film formed over the surface of the siliconsubstrate 500 was removed with use of diluted hydrofluoric acid.

By the XPS measurement, it was observed that silicon was included, at1.1 at. %, in the IGZO film deposited with use of the target to whichSiO₂ was added at 2 wt. %.

According to the above, when impurities such as silicon enter, by mixingor the like, the oxide semiconductor film in the vicinity of theinterface with the gate insulating film, crystallization of a channelformation region in the oxide semiconductor film is potentiallyinhibited. As a result, this example shows that it is important toreduce the concentration of silicon in the oxide semiconductor film inthe vicinity of the interface with the gate insulating film.

EXPLANATION OF REFERENCE

100: substrate, 101: gate electrode, 102: gate insulating film, 103:oxide semiconductor film, 103 a: region, 103 b: region, 103 c: region,105 a: source electrode, 105 b: drain electrode, 107: insulating film,108: channel protective film, 109: protective insulating film, 110:transistor, 120: transistor, 130: transistor, 200: silicon substrate,202: silicon oxide film, 204: IGZO film, 300: glass substrate, 302:silicon oxynitride film, 304: IGZO film, 400: glass substrate, 402: IGZOfilm, 500: silicon substrate, 502: IGZO film, 2700: e-book reader, 2701:housing, 2703: housing, 2705: display portion, 2707: display portion,2711: hinge, 2721: power switch, 2723: operation key, 2725: speaker,2800: housing, 2801: button, 2802: microphone, 2803: display portion,2804: speaker, 2805: camera lens, 2806: external connection terminal,3001: main body, 3002: housing, 3003: display portion, 3004: keyboard,3021: main body, 3022: stylus, 3023: display portion, 3024: operationbutton, 3025: external interface, 3051: main body, 3053: eyepiece, 3054:operation switch, 3056: battery, 4001: substrate, 4002: pixel portion,4003: signal line driver circuit, 4004: scan line driver circuit, 4005:sealant, 4006: substrate, 4008: liquid crystal layer, 4010: transistor,4011: transistor, 4013: liquid crystal element, 4015: connectionterminal electrode, 4016: terminal electrode, 4019: anisotropicconductive film, 4021: insulating layer, 4030: electrode layer, 4031:electrode layer, 4032: insulating film, 4033: insulating film, 4034:insulating film, 4510: partition wall, 4511: electroluminescent layer,4513: light-emitting element, 4514: filler, 4612: cavity, 4613:spherical particle, 4614: filler, 4615 a: black region, 4615 b: whiteregion, 9600: television set, 9601: housing, 9603: display portion,9605: stand

This application is based on Japanese Patent Application serial no.2011-215682 filed with Japan Patent Office on Sep. 29, 2011, the entirecontents of which are hereby incorporated by reference.

1. (canceled)
 2. A semiconductor device comprising: a gate electrode; agate insulating film over the gate electrode; an oxide semiconductorfilm over the gate insulating film; and a source electrode and a drainelectrode electrically connected to the oxide semiconductor film,wherein the oxide semiconductor film comprises indium, gallium and zinc,wherein the oxide semiconductor film comprises a region havingcrystallinity, wherein a concentration of silicon in the region havingcrystallinity is lower than or equal to 1.0 at. %, wherein aconcentration of carbon in the region having crystallinity is lower thanor equal to 1.0×10²⁰ atoms/cm³, and wherein the region havingcrystallinity comprises microcrystal.
 3. A semiconductor devicecomprising: a gate electrode; a gate insulating film over the gateelectrode; an oxide semiconductor film over the gate insulating film;and a source electrode and a drain electrode electrically connected tothe oxide semiconductor film, wherein the gate electrode comprises atleast one of molybdenum, titanium, tantalum, tungsten, aluminum, copper,neodymium, and scandium, wherein the oxide semiconductor film comprisesindium, gallium and zinc, wherein the oxide semiconductor film comprisesa region having crystallinity, wherein a concentration of silicon in theregion having crystallinity is lower than or equal to 1.0 at. %, whereina concentration of carbon in the region having crystallinity is lowerthan or equal to 1.0×10²⁰ atoms/cm³, and wherein the region havingcrystallinity comprises microcrystal.